Fracture behavior of P(VDF-TrFE)68/32 copolymer films under combined electrical and mechanical load

Mingzhi Zhang,Fei Fang,Wei Yang

2007-01-01

Abstract:The uniaxial tension fracture behavior with and without an electric field was characterized for P(VDF-TrFE)68/32 copolymer films prepared by stretching the solution-cast films. The results show that the film samples tensioned exhibited two-phase strengthening effect. The electric field applied parallel to the tensile axis enhances the yield strength while reduces the fracture strain. X-ray diffraction analysis demonstrated that the orientation degree of the molecular chain for the film sample tensioned under an electric field was smaller than that under pure mechanical tension. It is suggested that the electric field applied parallel to the tension direction caused the rotation of the molecular chain in the perpendicular direction, which prevented the films from acquiring a higher orientation degree of the molecular chain. Consequently, the post-yield strengthening process is restrained, resulting in a lower fracture strain and strength for the film samples uniaxial tensioned under an electric field.