Abstract:In this research, tri-block copolymer polycaprolactone-polybutadiene-polycaprolactone (PCL-PB-PCL) (Mn = 2382 g.mol−1) was synthesized via cationic ring-opening polymerization of caprolactone in the presence of hydroxyl-terminated polybutadiene (HTPB) as macroinitiator and different catalysts such as dibutyltin dilaurate, tin (II) 2-ethyl hexanoate, and tetra-n-butyl orthotitanate. This copolymer has a potential application in the propellant industries as a binder. The obtained products were characterized by FT-IR, and 1HNMR spectroscopy gel permeation chromatography (GPC). The thermal behavior of the tri-blockcopolymer was studied by thermogravimetry analysis (TGA) and differential scanning calorimetry (DSC). The result was approved that the glass transition temperature of the tri-block copolymer (Tg = −72.1 °C) is lower than homopolymer PCL (Tg = −65 °C). The effect of heating rate (5,7,10 and 15◦C min−1) on the decomposition of the copolymer was investigated. The kinetic parameter (activation energy for the thermal decomposition of tri-block copolymer) was calculated by the Flynn–Wall–Ozawa (FWO) and Kissinger methods. The polyurethane elastomers were synthesis by the reaction of triblock copolymer and toluene-2,4-diisocyanate diisocyanate(TDI) or isophorone diisocyanate(IPDI) isocyanates with different NCO/OH ratios and in the presence of the plasticizer. The plasticized elastomer with TDI and NCO/OH = 1.2 showed better mechanical properties than IPDI with 0.44 MPa strain and 483% elongation. The average value of the three tensile tests reported as the final result. The effect of 1,4 butanediol as chain extender on mechanical properties of polyurethane-based PCL-PB-PCL was investigated using a tensile test. According to the results, chain extenders caused increasing strength of plasticized elastomer (0.593 MPa) and decreasing its elongation at break (349%).

CHARACTERIZATION AND TERPOLYMERIZATION OF CARBON DIOXIDE/1,2-BUTYLENE OXIDE/ε-CAPROLACTONE

Synthesis And Properties Of Long Chain Polyesters From Biobased 1,5-Pentanediol And Aliphatic Alpha,Omega-Diacids With 10-16 Carbon Atoms

Crystallization Behavior and Mechanical Properties of Poly(Epsilon-Caprolactone)/Cyclodextrin Biodegradable Composites

Cobalt(III)‐complex‐mediated Terpolymerization of CO2, Styrene Oxide, and Epoxides with an Electron‐donating Group

Facile Synthesis of Functional Poly( Ε -Caprolactone) Via Janus Polymerization

Random Terpolymer of Carbon Dioxide, Butadiene and Epoxides: Synthesis, Functionalization and Degradability

All-natural environmentally degradable poly (butylene terephthalate- co -caprolactone): A theoretical and experimental study of its degradation properties and mechanisms

Effect of Composition on the Crystallization, Water Absorption, and Biodegradation of Poly(ε-caprolactam -co-ε-caprolactone) Copolymers

Zwitterionic Copolymerization of Γ-Butyrolactone with 3,3-Bis(chloromethyl) Oxacyclobutane Catalyzed by Scandium Triflates

Synthesis, Characterization, and Properties of Degradable Poly(l‐lactic Acid)/poly(butylene Terephthalate) Copolyesters Containing 1,4‐Cyclohexanedimethanol

Synthesis and Characterization of Biodegradable &Amp;epsilon;-Caprolactone/d,l-lactide Copolymer

Synthesis and Properties of Modified Biodegradable Polymers Based on Caprolactone

Efficient and Scalable Synthesis of CO2‐Based Polycarbonate Diols With Difunctional Initiator and Proton Exchange Agent

Degradability of Poly(epsilon-caprolactone) Bearing Pendant Carboxyl Groups

Synthesis and thermal decomposition kinetics of tri-block copolymer ε-caprolactone / polybutadiene (PCL-PB-PCL); preparation of polyurethane network-based tri-block copolymer

Synthesis and Characterization of Poly(ε‐caprolactone‐co‐δ‐ Valerolactone) with Pendant Carboxylic Functional Groups

Synthesis and Characterization of Graft Copolymers Poly(ethylene Oxide)-G-[poly(ethylene Oxide)-B-poly(ε-caprolactone)] with Double Crystallizable Side Chains

Preparation and Polymerization Mechanism of Dihydroxy-Capped PCL, Poly(cl- B -PEG- B -CL) and Poly(dtc- B -CL- B -DTC)

Aspergillus oryzae lipase-mediated in vitro enzymatic degradation of poly (2,2′-dimethyltrimethylene carbonate-co-ε-caprolactone)

[Current theories on the origin of cholesteatoma].

Synthesis, Characterization, and in Vitro Degradation of Star‐shaped P(ε‐caprolactone)‐b‐poly(L‐lactide)‐b‐poly(D,L‐lactide‐co‐glycolide) from Hexakis [p‐(hydroxymethyl)phenoxy]cyclotriphosphazene Initiator