REFINEMENT OF GRAIN AND ENHANCEMENT OF IMPACT TOUGHNESS FOR LOW-ALLOYING ULTRA-HIGH STRENGTH BAINITE STEELS

Gao Kuan,Wang Liuding,Zhu Ming,Chen Jingdong,Shi Yijun,Kang Mokuang
DOI: https://doi.org/10.3321/j.issn:0412-1961.2007.03.018
IF: 1.797
2007-01-01
ACTA METALLURGICA SINICA
Abstract:Through adding Si, Mn and Ni into low alloy ultra high strength bainitic steels (LUHSBS) and controlling the transformation temperature, cooling and tempering parameters the impact energy absorption (A(KV) >= 185 J) has been tripled compared to the martensitic steel 23MnNiCrMo with the same strength level (> 1500 MPa). The basic reasons of the excellent combination of strength and toughness consist in the refinement of microstructure, the increase of carbon content in the bainitic ferrite (BF), the elimination of carbides and the thin film shaped retained austenite (Art) with high volume fraction and stability. AFM and STM revealed that no bulky A(R) existed in the structure which will reduce the impact toughness of bainitic steels. Not only the shear-units are significantly refined, but also the average size of super-fine grains is less than 20 nm and the average thickness of partial shear-units in a BF lath is only about 1.6 nm. The refinement of microstructure, the enrichment of carbon atom in BF and the increase of both the dislocation density and the volume fraction of AR are the factors affecting the ultimate tensile strength, the stability of AR, and the impact toughness. Furthermore, the physical mechanism on the improvements of strength and toughness was discussed.
What problem does this paper attempt to address?