Abstract:The hot deformation behavior of a powder metallurgy (P/M) Ni-base superalloy FGH96 was investigated at the temperature (T) of 1050–1140°C, strain rate (ε˙) of 0.002–1.0s−1, and the height reduction of 20–50% via isothermal hot compression experiment. The flow behavior and the microstructural mechanism of the synthesized superalloy were systematically studied. The processing map was constructed based on the experiment data to evaluate the efficiency of power dissipation and recognize the instability regimes for forging process determination. The processing map with the strain of 0.15 exhibits a smooth and small variation of η and predicts a little instability regime confined at (T: 1050°C, ε˙:1.0 s−1), attributed to the previous particle boundary (PPB) cracks. The map obtained at the strain of 0.65 reveals a large domain with the efficiency above 40% and predicts two instability regimes at around (1050°C, 1s−1) and located in the regime of (T: 1080–1140°C, ε˙:0.002−0.01 s−1), respectively. The optimum processing condition is identified as (T: 1140°C, ε˙:1.0 s−1), which presented the highest efficiency in hot working process, as well as the obtained fine microstructure after the hot processing. Via microstructure characterization and observation, it is concluded that the dynamic recrystallization (DRX) occurred at the PPBs in the P/M superalloy. The DRX and the strain rate sensitivity exponent m are both affected by true strain. The local DRX presents a relatively low m in a small strain compression. With an increase of strain, the fraction of the recrystallized grains increases with m. The global DRX, however, presents a relatively high m in a large strain compression. It is thus indicated that the superplasticity of FGH96 superalloy can be realized at a slow strain rate such as 0.001s−1 and the deformation temperature of 1110°C, near to the γ′-transus temperature, by using the uniformly fine-grained superalloys as well as the high temperature superplastic forming equipment.

Determining Processing Maps of FGH96 Superalloy

Investigation on hot deformation behavior of P/M Ni-base superalloy FGH96 by using processing maps

Hot Deformation Behavior and Hot Processing Map of GH2907 Superalloy

Flow Behavior and Processing Map of FGH96 Superalloy During Two-Pass Hot Deformation

Study on Constitutive Relationships and Processing Maps for FGH96 Alloy During Two-Pass Hot Deformation

Study on Hot Deformation Behavior of P/M Superalloy Using Processing Map

Flow Behavior for FGH96 Superalloy during Two-Pass Hot Deformation and Constitutive Relationship

Efficiency of Power Dissipation and Instability Criterion for Processing Maps in Hot Forming

Flow Behavior Study on Fine-Grain FGH96 P/M Superalloy During Hot Deformation

Hot Compressive Deformation Behavior and Microstructure Evolution of HIPed FGH96 Superalloy

Hot Deformation Behavior and Processing Map of a Nickel-Base Superalloy GH4169

Simulation of the FGH96 Superalloy Microstructural Changes under Different Deformation Conditions

Constitutive Behavior and Processing Maps of Low-Expansion GH909 Superalloy

Deformation and microstructural evolution in alloy FGH96 under isothermal forging conditions

Tensile and low cycle fatigue properties of nickel-base powder metallurgy superalloy FGH95

Finite Element Simulation Of Superplastic Isothermal Forging Process For Nickel-Base Pm Superalloy

Characterization of hot deformation behavior and processing map of FGH4096–GH4133B dual alloys

Constitutive Equation for Hot Deformation and Hot Processing Map of Wrought GH4169 Superalloy

Investigation on Hot Deformation Behavior of P/M Superalloy FGH4096

Failure behaviors and processing maps with failure domains for hot compression of a powder metallurgy Ni-based superalloy

Hot deformation behavior and new grain size model of hot extruded FGH4096 superalloy during hot compression