Abstract:Summary Asphalt road gradually deteriorates in serviceability with insignificant damage. The deterioration begins with microcracks and continues until structural failure. To facilitate early damage prediction, this study proposes a structural self‐sensing technique based on the piezo‐resistive behavior of conductive asphalt concrete. To this end, conventional asphalt mixtures were modified into self‐sensing mixtures by adding conductive carbon fiber (CF) and iron tailings aggregates (TA) as alternatives for natural aggregates (NA). The self‐sensing response was evaluated by correlating fractional changes in electrical resistance (FCR) with the deformation of mixture within and beyond the elastic regime in response to varying stress amplitudes under fatigue cyclic compressive loading. From the results, it can be seen that the mixture exhibits sufficient mechanical strength and low resistivity to achieve a self‐sensing response. Furthermore, the self‐sensing response varies significantly with the stress amplitude. The mixture exhibits sufficient sensitivity to the compaction and deformation within the elastic regime by reversibly decreasing its electrical resistance at low‐stress, manifested as increase in negative (−) FCR. The −FCR reversibly decreases, reflecting initiation of microcracks due to increased deformation within the elastic regime at medium‐stress. However, irreversible FCR is observed at high‐stress due to increase in deformation beyond the elastic regime, which leads to fracture. After fracture, the mixture does not show sensitivity to stress and deformation owing to the cracking of internal conductive network. In conclusion, the mixture provides early damage prediction as sensitive damage sensor in the elastic regime and enables real‐time structural health monitoring (SHM) of asphalt pavements.

Stress Concentration Factor As a Performance Indicator for Asphalt Mixes

Inverse Engineering Stress-Dependent Resilient Moduli of Cement-Treated Base Materials in Asphalt Pavements Using Falling Weight Deflectometer

Evaluation of Complex Poisson’s Ratio of Aged Asphalt Field Cores Using Direct Tension Test and Finite Element Simulation

Mechanistic Characterization of Fatigue Damage Process and Failure Predictions of Asphalt Binders

Micromechanics Modeling of Viscoelastic Asphalt-Filler Composite System with and Without Fatigue Cracks

Three-Dimensional Discrete Element Modelling Of Influence Factors Of Indirect Tensile Strength Of Asphalt Mixtures

A Research on Fatigue Damage Constitutive Equation of Asphalt Mixture

Micromechanical Analysis of Asphalt-Mixture Shear Strength Using the Three-Dimensional Discrete Element Method

Pseudo Energy-Based Crack Initiation Criterion for Asphalt-Filler Composite System under a Fatigue Shear Load

Micromechanical Discrete Element Modeling of Asphalt Mixture Shear Fatigue Performance

STUDY ON STRESS INTENSITY FACTOR AFFECTED BY FRICTION COEFFICIENT BETWEEN SURFACE LAYER AND SUBBASE

Three-Dimensional Discrete-Element Modeling of Aggregate Homogeneity Influence on Indirect Tensile Strength of Asphalt Mixtures

Research on Design Parameters for Fatigue Performance of Asphalt Mixtures

Numerical Analysis for Basalt Fiber Reinforced High-Viscosity Asphalt Concrete Bridge Deck Pavement

Viscoelastic Fracture Analysis of Asphalt Concrete Pavement with Cracks

Three-Dimensional Micromechanical Simulation and Evaluation of High-Toughness Ultra-Thin Friction Course with X-Ray Computed Tomography

Fatigue Performance Analysis of Fine Aggregate Matrix Using a Newly Designed Experimental Strategy and Viscoelastic Continuum Damage Theory

Evaluation of Fatigue Behavior of Asphalt Field Cores Using Discrete Element Modeling

Parameter Optimisation of a 2D Finite Element Model to Investigate the Microstructural Fracture Behaviour of Asphalt Mixtures

Self‐stress and deformation sensing of electrically conductive asphalt concrete incorporating carbon fiber and iron tailings

Multi-scale finite element simulation of asphalt mixture anti-cracking performance