Abstract:In the present study, Er 3+ -Yb 3+ co-activated multicomponent phosphate glasses were prepared by conventional melt quenching technique. The x-ray diffraction analysis confirmed the amorphous nature of all the samples. Field emission scanning electron microscopy of the glasses revealed homogeneous and smooth morphology. Moreover, the EDAX results confirmed the existence of phosphate, oxygen, aluminum, sodium, potassium, barium, erbium, and ytterbium in the glass matrix. The optical properties were determined and the absorption coefficient was calculated using absorbance spectrum, which contains 11 bands attributed to the transitions from the ground state 4 I 15/2 up to the various higher states 4 I 13/2 , 4 I 11/2 , 4 I 9/2 , 4 F 9/2 , 4 S 3/2 , 2 H 11/2 , 4 F 7/2 , 4 F 5/2 , 2 G 9/2 , 4 G 11/2 , and 4 G 9/2 , respectively. The mentioned bands' presence is due to energy levels reported for Er 3+ ion glass systems. However, the band around 970 nm is corresponding to 2 F 7/2→ 2 F 5/2 (Yb 3+ ) and 4 I 11/2→ 4 I 15/2 (Er 3+ ) Er 3+ intra-4F-transition of erbium ions. The radiative properties for the metastable level 4 I 13/2 were determined by virtue of the Judd–Ofelt theory. The τ r slightly decreases with the increase in Yb 3+ ion sensitizer, and it has maximum value equal to (11.49 ms) for PANBK0.5Er0.5Yb sample. This study introduced promising results to be applied in laser as well as wave guide optical amplifiers' applications around 1.5 μm, with higher intensity emission bands by doping the prepared sample with 0.5 mol% Er 3+ –0.75 mol% Yb 3+ ions. The PL results in the NIR region at 1.5 μm leading to higher intensity of PANBK0.5Er0.75Yb sample support wave guide optical sensor system application.

Optical Transition Probability of Er3+ Ions in Er3+/Yb3+ Codoped Ca3Ln2(BO3)4 (ln=y, Gd, La) Crystals

Judd–Ofelt analysis and upconversion emission of Er 3+ –Yb 3+ co-doped oxyfluoride glass ceramics containing LaF 3 nanocrystals

Chemical Combustion Synthesis and Up-Conversion Properties of Er3+ Doped Yb3Al5O12 Powder

Spectroscopic Properties Of Er3+/Yb3+ Co-Doped 50sio(2)-20al(2)O(3)-30caf(2) Glass And Glass Ceramics

Spectroscopic properties of Er<sup>3+</sup>and Yb<sup>3+</sup>co-doped glass ceramics containing SrF<sub>2</sub>nanocrystals

Spectroscopic Properties Of Er3+ And Yb3+ Co-Doped Glass Ceramics Containing Srf2 Nanocrystals

Research on optical properties of Yb3+/Er3+ co-doped oxy-fluoride glass

Intense Upconversion Luminescence of Er3+/Yb3+ Codoped Oxyfluoride Borosilicate Glass Ceramics Containing Ba2GdF7 Nanocrystals

Spectroscopic Properties of Er3+/Yb3+ Co-Doped 50sio2–20al2o3–30caf2 Glass and Glass Ceramics

[Spectra of Ce3+, Tb3+ and Gd3+ Ions in Ln(BO3,PO4) [ln = La, Y]].

Spectroscopic Properties of Er3+–Yb3+ Co-Doped Glass Ceramics Containing BaF2 Nanocrystals

Upconversion Luminescence Properties of Er3+ Doped Yb2ti2o7 Nanophosphor by Gd3+ Codoping

Optical transition and near-infrared upconversion luminescence properties of YNbO4: Er3+, Yb3+ phosphors

Synthesis and upconversion luminescent properties of Er 3+ doped and Er 3+-Yb 3+ codoped GdOCl powders

Optical Properties of Er3+-Yb3+ Ions Co-activated Multicomponent Phosphate Glasses for Near-Infrared Applications

Spectroscopic properties of Er3+/Yb3+ co-doped fluoro bismuth borate glasses for up-conversion luminescence

Infrared cross-section measurements for crystals doped with Er/sup 3+/, Tm/sup 3+/, and Ho/sup 3+/

Effect of Ca2+ ions on structure and spectroscopic properties of Er3+: KBaY(MoO4)3 crystals

Interionic distance distributions between $Er^{3+}$ and $Yb^{3+}$ as dopants in some crystal matrix hosts used for upconversion luminescence

Spectroscopy, Crystal-Field, and Transition Intensity Analyses of the C$_{\rm 3v}$(O$^{2-}$) Centre in Er$^{3+}$ Doped CaF$_{2}$ Crystals

The synthesis, crystal structure and multicolour up-conversion fluorescence of Yb3+/Ln3+ (Ln = Ho, Er, Tm) codoped orthorhombic lutetium oxyfluorides