Abstract:Concrete-filled double-skin steel tubular (CFDST) specimens that exhibit lightweight, good ductility, and better bending resistance, can be used for beams. However, fire often causes great damage, and the flexural behavior of CFDST beams after subject to high-temperature has not been studied. To investigate the flexural behavior of CFDST beams after subject to high temperature, seven CFDST specimens after subject to high temperature were carried out four-point bending tests. The main parameters explored in the test include hollow ratio (0.31, 0.52, 0.72) and temperature (300 °C, 500 °C, 800 °C). The corresponding finite-element analysis (FEA) models were established, and the results showed good agreement with the test. The in-depth mechanism and systematic analysis including the influence of different hollow ratio, material property, and temperature on the whole process curve of CFDST after subject to high temperature are carried out using FEA models. It is found that the ultimate bending moment of CFDST after subject to high-temperature increases with hollow ratio and material property, but decreases with the temperature. The outer steel tube contributes the most to the ultimate bending moment, and the inner steel tube improves the ductility at a later stage. Specimens with a large hollow ratio (χ ≥ 0.52) have better bending capacity, and the ultimate bending moment of specimens with a small hollow ratio (χ < 0.52) decrease the least with the change of temperature due to the protection of concrete. Based on the findings from the test and numerical studies, a temperature effect coefficient kr is proposed to represent the residual bearing capacity after subject to high temperature, and combined with three different codes to evaluate the ultimate bending moment. A comparison of test results showed the calculated results following the T/CCES 7–2020 (2020) had a good agreement.

Experimental research on impact-resistant capacity of concrete filled steel tube under high temperature

EXPERIMENTAL RESEARCH ON IMPACT BEHAVIOR OF CONCRETE-FILLED STEEL TUBE AT ELEVATED TEMPERATURES

Tests on impact behaviour of concrete-filled steel tube after exposure to high temperatures

Tests on Impact Behaviour of Micro-Concrete-filled Steel Tubes at Elevated Temperatures Up to 400°C

Impact Behaviours Of Concrete-Filled Steel Tubular Stub Column At Elevated Temperatures

Strength of Concrete Filled Steel Tubes under High-Strain Rate Loading

Experimental study on dynamic behavior of concrete at elevated temperatures

Experimental Studies on Concrete Filled Steel Tubes under High Strain Rate Loading

Behavior Of Concrete Filled Tubes And Confined Concrete Filled Tubes Under High Speed Impact

Flexural behavior of concrete-filled circular steel tubes under high-strain rate impact loading

Effects of Sustained Pre-Load on Residual Strength and Stiffness of Concrete-Filled Steel Tube after Exposure to High Temperatures

Axial Impact Behaviors of Stub Concrete-Filled Square Steel Tubes

Impact Behaviors of CFT and CFRP Confined CFT Stub Columns

Axial Impact Behavior of Confined Concrete Filled Square Steel Tubes Using Fiber Reinforced Polymer

Behaviour of CFT and CCFT columns under impact loads

High-strain Rate Compressive Behavior of CFRP Confined Concrete: Large Diameter SHPB Tests

Compressive Impact Tests of Lightweight Concrete with 155-Mm-diameter Spilt Hopkinson Pressure Bar

Experimental and numerical study on the impact performance of concrete-filled high-strength steel tube (CFHSST)

The lateral impact performance of concrete-filled steel tubular (CFST) members at high temperatures

Flexural behavior of concrete-filled double-skin steel tubular beams after subject to high temperature

Behaviour of high-strength concrete filled steel tubes under transverse impact loading