Enhanced Hot Workability of Ti–46Al–4Nb–0.1B Alloy by Introducing Adjustable β Phase via Elemental Powder Metallurgy
Qi Wang,Guo-qing Chen,Huaping Tang,Xue-song Fu,Wen-long Zhou
DOI: https://doi.org/10.1002/adem.202000762
IF: 3.6
2020-09-02
Advanced Engineering Materials
Abstract:<p>TiAl‐base alloys are a kind of promising materials for high‐temperature applications. The β phase existing in TiAl alloy can improve the hot‐workability, but deteriorates the creep properties. Preparing a β phase‐containing TiAl base alloy to enhance the hot‐workability before hot deformation and eliminating the β/B2 phase by post‐heat treatment to improve the service performance is a good strategy. In this paper, a significant volume fraction of β phase was obtained in the Ti‐46Al‐4Nb‐0.1B alloy by the elemental powder metallurgy (EPM), and the β/B2 phase was eliminated by the subsequent heat treatment. The results demonstrate that the microstructure of the EPMed Ti‐46Al‐4Nb‐0.1B alloy predominantly consists of α<sub>2</sub>/γ lamellar colonies, equiaxial γ grains, and some randomly distributed β phase and σ‐Nb<sub>2</sub>Al phase. The β/B2 phase formed at the Nb‐enriched regions caused by insufficient diffusion. The EPMed Ti‐46Al‐4Nb‐0.1B alloy had a relatively low thermal deformation activation energy (<i>Q</i>, 410 kJ/mol), showed a well hot‐workability. The existence of the β phase is advantageous to harmonize the deformation of α<sub>2</sub>/γ lamellar grains and to improve the deformability of the TiAl alloy. The subsequent heat treatment can eliminate the Nb‐enriched regions and the B2 phase to ensure good service performance.</p><p>This article is protected by copyright. All rights reserved.</p>
materials science, multidisciplinary