Effect of Substituting Nd for Y on Microstructure and Mechanical Properties of Mg-7Y-2Al Alloy
Lili Zhao,Yicheng Feng,Liping Wang,Lei Wang,Rui Fan,Tao Ma,Sicong Zhao
DOI: https://doi.org/10.1007/s11665-023-08277-7
IF: 2.3
2023-05-13
Journal of Materials Engineering and Performance
Abstract:This study investigated the microstructure and mechanical properties of Mg-(7-x)Y-xNd-2Al (x = 0, 2, 4, 6) alloys with rare earth (RE) element Nd instead of Y. The results reveal that the substitution of Nd for Y promotes the formation of the Al-RE phase and Mg-RE eutectic phase in the as-cast alloy. Furthermore, after solution treatment, all eutectic phases dissolve into the α-Mg matrix, while the Al-RE phase (Al 2 RE phase) does not dissolve. Additionally, the lamellar Al 2 RE phase precipitates in the grains of the Nd-containing alloy. The age-hardening curve indicates that when Nd is substituted for Y, the peak-aging time is reduced and the peak hardness increases. Moreover, Nd promotes the precipitation of the nanometer β′′ phase during aging, which improves the mechanical properties of the alloy. The best peak-aging yield strength, tensile strength, and elongation of the 4% Nd alloy are 182, 285 MPa, and 7.4%, respectively.
materials science, multidisciplinary