Cellular compatibility of deproteinized bone as scaffold in vitro

K Cao,W Fan,H An,DM Jiang,Y Shu,ZM Han

DOI: https://doi.org/10.3321/j.issn:1673-8225.2007.35.005

2007-01-01

Abstract:AIM: Natural bone has been made into deproteinized bone (DPB) successfully by hydrogen dioxide and diethyl ether method. In this study, the cellular compatibility of DPB as bio-scaffold co-cultured with osteoblast in vitro was investigated, so as to provide good scaffold material for bone construction in tissue engineering. METHODS: The experiment was conducted in the Experimental Animal Center of Chongqing University of Medical Sciences from January 2003 to December 2005. ①Osteoblasts were collected from the rabbit fetus skull by collagenase digestion associated with tissue nubbles cultivation and cultured in vitro. The skull of New Zealand White fetus rabbit was cut into 2 mm ×2 mm bone blocks which were digested with collagenase Ⅰ at room temperature. Then the bone blocks were cut into 1 mm ×1 mm smaller ones and incubated. After the cultured cells covered the block interspace, cells were subcultivated and identified by morphological characteristics, by alkaline phosphatase cytochemistry staining and calcium tubercle staining. The third generation cells were thawed and cultured, subsequently suspended at a concentration of 2×1010/L for implantation. ②The fresh metaphyseal cancellous bone of adult New Zealand white rabbits was processed into DPBs with hydrogen dioxide and diethyl ether. The DPB scaffolds were immersed by prepared cell suspension then co-cultured subsequently in vitro. The cellular compatibility of DPB was detected by enzyme digestion, inverted phase contrast microscopy and scanning electron microscopy. RESULTS: ①Osteoblasts were obtained successfully from the rabbit fetus skull by collagenase digestion associated with tissue nubbles cultivation. Primary cells presented irregular polygonal, while all subcultivated ones were long spindle-shaped or long irregular polygonal under inverted phase contrast microscope. Most cells were positive black in alkaline phosphatase cytochemistry staining test and considerable black calcified nudes distributed in extracellular matrix after calcium tubercle staining. ②The logarithmic growth phase of osteoblasts started at the 3rd day after the co-culture in vitro. Under inverted phase contrast microscope, osteoblasts increased obviously accompanied with discovery of cellular connective development at the 7th day after implantation. Under scanning electromicroscope, obvious connective and fused development form of osteoblasts was discovered at the 7th day after implantation. CONCLUSION: DPB prepared with hydrogen dioxide and diethyl ether processes satisfactory cellular compatibility, and it could serve as bio-scaffold of tissue engineered bone.