Experimental study on xenogeneic bone prepared with deproteinization and freeze-drying method

JIE Yong-sheng,QI Hui,CHEN Lei,GAO Xin-sheng,SUN Lei

DOI: https://doi.org/10.3969/cmba.j.issn.1673-713X.2013.05.002

2013-01-01

Abstract:Objective To study the mechanical property and antigenicity of bovine cancellous bone after deproteinization and freeze-drying, and to determine the possibility of applying it as the scaffold of bone transplantation. Methods Bone particles and sticks of cancellous bone from bovine furmer were made with deproteinization with the liquid of sodium dodecyl benzene sulfonate(ABS) and anionic surfactant sodium fatty alcohol ether sulfate(AES) and distilled water in a ratio of 13:7:80(weight). And sonic oscillation was used to further eliminate the residual protein in cancellous particles and sticks. The bone structures were observed under electron microscope. Hemolytic, cytotoxic and bone-implantation tests were examined to determine the histocompatibility of this kind of xenogeneic bone, and the mechanical property was also measured and compared with bovine cancellous particles. The porosity was examined with liquid discharge method. Results It showed that deproteinized cancellous bone maintained natural network pore system. No obvious cytotoxicity and hemolysis was observed. As found by bone-implantation test, bone sticks were fused with the peripheral bone of the rabbit only after implantatation of 4 weeks, and were completely absorbed after 52 weeks. The porosity was over 60%. Conclusion This kind of xenogeneic bone has good histocompatibility and mechanical property, and is a proper scaffold of bone transplantation with deproteinization and freeze-drying method.