Abstract:The fracture behaviour of compact tension (CT) specimens made of nickel-based single crystal superalloys DD3 has been studied by experiments at 760, 850 and 950°C. Three different crack crystallographic orientations, (001)[100], (011)[100] and (111)[0−11], of the specimens have been considered. The macro crack growth and micro characteristics of the fracture surfaces have been examined by optical microscope (OM) and scan electron microscope (SEM). The emphasis has been put on the crack growth path and fracture toughness as well as the micro characteristics of the fracture surface. The crystallographic plastic finite element method (FEM) has also been used to analyze the resolved shear stress distribution, normal stress and slip systems activated of the specimens, especially ahead of the cracks, in order to have a deep understanding with crack. The experimental and FEM results show that the crystallographic orientations of the CT specimens have a great influence on the crack growth path and fracture toughness of the specimens as well as the stress characteristics ahead of the cracks. The experiments show that at low temperature, e.g. 760 and 850°C, the macroscopic crack growth path appears as zigzag wave, while at high temperature, e.g. 950°C, all the fracture surfaces are flat along the crack direction except the crack initiation. FEM analysis shows that deformation and fracture ahead of the crack take place in specific slip planes in different crack orientations. The resolved shear stress of the slip system is found to be the main factor of specimens fracture. Also, the normal stress of slip planes has some influence on the crack growth. To the three specimens tested at 760°C, the deflected angles of crack initiation direction with respect to crack plane are 45°, 53.7°and 90° in the order of crack orientations of (001)[100], (011)[100] and (111)[0−11]. The growth path of the crack observed in experiment is agreement with the theoretical analyses by FEM. Furthermore, temperature is the other factor affecting the fracture of specimens. It is clear that the fracture mode of the CT specimens transfers from brittle to ductile with the temperature increasing.

Fracture Behaviour of Compact Tension Specimens of Nickel-based Single Crystal Under Tension Creep and Cyclic Loading

Fracture Behaviour of the Compact Tension Specimens of Nickel-Based Single Crystal Superalloys at High Temperatures

Crack propagation paths and fracture of Ni-based single crystal

Creep Behaviors of Nickel-Based Single Crystal Superalloys Compact Tension Specimen at High Temperature

Creep-fatigue Behavior of Nickel-Based Single Crystal Superalloy with Different Orientations: Experimental Characterization and Multi-Scale Simulation

Investigation on Microstructure Evolution and Fracture Morphology of Single Crystal Nickel-Base Superalloys under Creep-Fatigue Interaction Loading

Anisotropic Creep Damage and Fracture Mechanism of Nickel-Base Single Crystal Superalloy under Multiaxial Stress

Creep damage and crack initiation behaviour of nickel-base single crystalline superalloys compact tension specimen with a void ahead of crack tip

Effects of Tensile/compressive Creeps on Microstructure Evolution of Nickel-Based Single Crystal Superalloys

Microstructure Evolution Mechanisms in Nickel-Based Single Crystal Superalloys under Multiaxial Stress State

Fracture Toughness Analysis of Anisotropic Nickel-Based Single Crystal Superalloys at High Temperature

Low Cycle Fatigue Failure Analysis of a Ni‐Based Single Crystal Superalloys at 850 °C

Anisotropic Creep Life Prediction of Nickel-based Single Crystal Based on Dislocation Movement

Transient Thermal Fatigue Crack Propagation Behavior of a Nickel-Based Single-Crystal Superalloy

Microscopic Damage and Fracture Mechanism of Nickel-based Single Crystal Superalloy during Low Cycle Fatigue at Elevated Temperature

Numerical simulation on creep damage and crack initiation behaviour of nickel-based single crystal superalloys containing a casting void

Microstructure Characterization and Damage Coupled Constitutive Modeling of Nickel-Based Single-Crystal Alloy with Different Orientations

Creep Residual Life Prediction of a Nickel-Based Single Crystal Superalloy Based on Microstructure Evolution

Fracture Behavior of the Compact Tension Specimens in NiTi Shape Memory Alloys

Investigation on low cycle fatigue of nickel‐based single crystal turbine blade in different regions

A Crystallographic Model for the Orientation Dependence of Low Cyclic Fatigue Property of a Nickel-Base Single Crystal Superalloy