Zinc phosphate film and cathodic electro-coat deposition on magnesium alloy

Jian-she LIAN,Guang-yu LI,Li-yuan NIU

DOI: https://doi.org/10.3969/j.issn.1671-7775.2007.01.010

2007-01-01

Abstract:An uniform and fine zinc phosphate film on AZ91D magnesium alloy was prepared by using a phosphating bath containing Ce(NO_3)_3 and a corrosion inhibitor.The experimental results showed that the addition of Ce(NO_3)_3 in the phosphating bath made phosphate film finer and non-crack.Very dense phosphate coating was obtained from the phosphating bath containing 1.5 g/L Ce(NO_3)_3.Cathodic electro-paint was then coated on the phosphated magnesium alloy.The addition of Ce(NO_3)_3 also reduced the weight loss of phosphate coating during the electro-coating and drying processes.The cathodic electro-coat of 35 μm thickness plus phosphate coating on the AZ91D magnesium alloy can bear 1 000 h salt fog test without corrosion.It is thus concluded that the zinc phosphate film+cathodic electro-paint is an effective technique for protection of magnesium alloy.