Abstract:In this paper, an acrylate copolymer-based oil adsorption resin was designed and synthesized by a suspension polymerization with octadecyl acrylate (SA) and butyl acrylate (BA) as monomers, divinylbenzene (DVB) as a cross-linking agent, and toluene as a pore-forming agent. By studying the synthesis conditions, the copolymer "SA-BA-DVB" (PSBA) with the best adsorption capacity was obtained, when the molar ratio between SA and BA was about 0.9, the content of the DVB and PVA 1788 was about 0.107 wt% and 1.0 wt%, respectively, accounting for the total mass amount of the monomers. Furthermore, by introducing 2% reactive silica nanoparticles (R-SiO2), the performances of the PSBA were improved due to its increased hydrophobicity and activity space. The equilibrium adsorption capacity of the resulted R-SiO2/PSBA to kerosene, diesel oil, benzene, and p-xylene was 31.90, 34.13, 39.44, and 41.81 mL/g, respectively, which is about 1.12 to 1.21 times higher than that of the PSBA. Also, the R-SiO2/PSBA show brilliant oil retention rate of about 99% after centrifugation at 3000 rpm for 5 min and recycling ability which can be reusable for at least 10 absorption-desorption cycles without capacity change, demonstrating that the obtained R-SiO2/PSBA resin can be used as oil removing agents in the field of oil spill applications.Highlights R-SiO2 modified acrylate copolymer as an oil adsorption resin was designed and synthesized. The influence of the monomers, cross-linking agent, and others on the adsorption resin was systematically studied. The adsorption kinetics and performances of the adsorption resin were studied. The synthesis process, water contact angles, and adsorption capacities of PSBA and R-SiO2/PSBA. R-SiO2/PSBA is superior to PSBA in hydrophobicity and adsorption capacity for benzene, p-xylene and disel.image

Synthesis and characterization of poly(styrene-methacrylate) highly oil absorptive resin

Synthesis of high oil-adsorption copolymer

Synthesis and Properties of Oil Absorption Resins Filled with Polybutadiene

Synthesis of Oil-Absorption Multi-Component Copolymer Resin

Synthesis and Properties of High Oil Absorptive Cross-Linked Lauryl Acrylate-Styrene-Egdma Copolymers

Oil‐absorption Function of Physical Crosslinking in the High‐oil‐absorption Resins

Effect of Styrene Dosage on Properties of Acrylic Oil Absorption Resin

Synthesis of a novel oil-absorption resin and optimization of its performance parameters using response surface design

Preparation and Performance Research of Highly Oil-Absorption Ternary Copolymer Resin

Comparison of Totally Chemical Crosslinking and Partially Physical Crosslinking of High Oil Absorption Resins

Synthesis of Acrylate Copolymer‐based Super Oil Adsorption Resins and Their Performances

Preparation of High Oil Absorption Resins by Suspended Emulsion Polymerization and Their Properties

Acrylate Copolymer-Based Super Oil Absorption Resins: Effects of Steric Hindrance of the Monomer

In-depth Investigation on the Factors Affecting the Performance of High Oil-Absorption Resin by Response Surface Method

Prepartion of New High-Oil-absorbing Resin

Synthesis and Characterization of A High Oil-Absorbing Magnetic Composite Material

Synthesis and Performance of A Self Crosslinkable Acrylate Copolymer with High Compatibility for an Oil Well Cement Modifier

Process Optimization of High Oil Absorption Resins by Suspended Emulsion Polymerization and Their Properties

Microwave Irradiation Syntheses and Properties of Polydodecylmethacrylate-2-ethyl Hexyl Acrylate Resin for the Adsorption of Oil Fume

SYNTHESIS AND PROPERTIES OF HIGH OIL-ABSORBENT POLY(VINYL CHLORIDE)-BUTYL ACRYLATE-DIVINYLBENZENE GRAFT COPOLYMER

Synthesis and characterization of reinforced acrylic-based superabsorbents crosslinked with divinylbenzene