Abstract:A surfactant-templated silica xerogel with high pore volume, high porosity and narrow bimodal mesopore size distribution (designated as BMS) was synthesized by a judiciously controlled two-phase sol–gel processing under basic conditions. The properties of BMS silica mesostructure and the effect of ammonia/silica molar ratio on the resultant silica structure and morphology were assessed using various analytical techniques such as XRD, 29Si MAS NMR, SEM, TEM, TG-DTA and N2 adsorption measurements. It is found that BMS silica xerogel consists of the packing of the micelle-encapsulated nanometer silica particles in the 20–40 nm range, depending upon the ammonia/silica molar ratio, and shows both an intraparticle framework mesopore resulting from the surfactant removal and a textural mesopore resulting from the interparticle voids, which can be adjusted in the 12.6–34.8 nm range by varying just the ammonia/silica molar ratio. The textural pore volumes for all BMS silica can be two or more times as large as the framework pore volumes, and the fill of a certain amount of surfactant between interparticle voids in as-synthesized BMS silica xerogel may play a crucial role for the formation, stability and ordering of textural mesoporosity. A fast hydrolysis and slow condensation process is beneficial to the formation of BMS silica mesostructure. Following a gradual increase of ammonia/silica molar ratio, thus an increase of condensation rate, the mesostructure evolution of the resultant silica products obtained from a bimodal mesopore via a disordered mesopore to a well-defined ordered hexagonal mesopore MCM-41 was observed.

Effect of the different silica sources on the synthesis mechanism of mesoporous V-MCM-41

INFLUENCE OF SILICA SOURCE ON THE CRYSTALLIZATION OF MORDENITE ZEOLITE

Influence of cations (Li+, Na+, K+)for synthesis mesoporous molecular sieve MCM-41 and their properties

Synthesis and properties of mesoporous molecular sieve MCM-41 from extreme dense system with auxiliary alkanes

Influences of anions X-(F-, Cl-, Br-) on synthesis and properties of mesoporous molecular sieve MCM -41

Influence of System Composition on Mesoporous Silica Materials Using Lamellar Liquid Crystals As Templates

The Effect of Al Content on the Pore Diameters of the Mesoporous Molecular Sieves Synthesized with Microcline as Starting Material

Synthesis of Si-based mesoporous materials with different structural regularity

Influence of synthesis parameters on the formation and structure of bimodal mesopore silica in a controlled sol-gel process

Mesoporous silica obtained with methyltriethoxysilane as co-precursor in alkaline medium

Synthesis and Characterization of Mesoporous Molecular Sieves MCM-41 Containing Hybrid Atoms

The Synthesis of Mesoporous Molecular Sieve MCM-48

Double-Mesopore V-Msu-X Silica and Its Pure Siliceous Derivative Prepared by One Synthesis System

Synthesis and properties of aluminosilicate mesoporous material with adjustable pore structure

Synthesis of Mesoporous Silica Using Triton X - 100 As Template and Study of the Morphology

Controlled Synthesis of Mesoporous Silicas Mcm-48 and Mcm-41 by Using Mixed Templates

A Reliable Synthesis of Cubic Mesoporous MCM-48 Molecular Sieve

Synthesis and Characterization of MCM-41 Molecular Sieves Nanoparticals

Synthesis and Coating of Ordered Mesoporous Silica

Influence of Organosiloxanes on the Properties of Mesoporous Materials.

Effects of Ammonia/silica Molar Ratio on the Synthesis and Structure of Bimodal Mesopore Silica Xerogel