Inelastic Neutron Scattering from CeOs<sub>4</sub>Sb<sub>12</sub>
Changping Yang,Masahumi Kohgi,Kazuaki Iwasa,Hitoshi Sugawara,Hideyuki Sato
DOI: https://doi.org/10.1143/JPSJ.74.2862
2005-01-01
Journal of the Physical Society of Japan
Abstract:Rare-earth filled skutterudites of the formula RT4X12 (R = rare earths, T 1⁄4 Fe, Ru, Os, X 1⁄4 P, As and Sb) are formed in a body-centered cubic LaFe4P12 structure with a space group of Im3. These compounds have been the focus of extensive efforts recently owing to their various electrical and magnetic properties, particularly, a novel mechanism of superconductivity observed in this series. Among them, most Ce-containing RT4X12 compounds are semimetals or semiconductors characterized by energy gap formation except CeRu4Sb12, which is a non-Fermi liquid. 4) CeOs4Sb12 is considered as a Kondo insulator and shows many interesting physical features determined by transport measurements, such as metal–insulator transition, magnetic moment markedly decreasing at low temperatures, and an unclear transition occurring below 0.86K. These notable features are attributed to the freedom and instability of 4f electrons of Ce3þ ion in CeOs4Sb12, which strongly correlate with on-site and inter site electrons or ions of its surroundings. In addition to the features of the magnetic 4f electrons, the lattice dynamics of filled skutterudites is also particularly interesting and vital because incoherent phonons, resulting from the unique rattling vibration mode of rare earth atoms, was claimed to have been observed in some skutterudite structures. In this work, we performed inelastic neutron scattering on the CeOs4Sb12 compound in order to study the 4f electron state as well as phonon state to understand the above-mentioned features. Single crystal samples were synthesized by the Sb-self-flux growth method using starting raw elements with an atomic ratio of Ce : Os : Sb 1⁄4 1 : 4 : 20, in which Sb was used much more than its stoichiometric amount in order to compensate for the flux consumption. Inelastic neutron scattering measurements of a powder sample prepared from single crystals with a weight of 60.7 g were performed using the pulsed-neutron spectrometers INC and LAM-D installed at the pulse neutron scattering facility KENS of KEK (High Energy Accelerator Research Organization) at Tsukuba, Japan. We also performed measurements for single crystals using triple-axis spectrometers of 6G and TAS-2 installed in the reactor JRR3M of JAERI (Japan Atomic Energy Research Institute) at Tokai Japan within the scattering plane with [001] and [110] crystallographic axes at room temperature. Figure 1 shows the inelastic neutron spectrum at a lowangle detector bank (2 1⁄4 5{9 ) measured using the chopper spectrometer INC of KEK with the incident neutron energy of 60meV for the CeOs4Sb12 powder sample. The spectrum is shown on the absolute scale of the cross section after calibration by the cross section of a standard vanadium sample. The dashed line shows the calculated cross section of CF (crystal field) excitations at 28.2meV for CeOs4Sb12 based on the model of the ground-state of doublet 7 and excited-state of 8 quartet proposed in ref. 5. It can be clearly seen from the figure that there is no such inelastic intensity except for a broad spectrum below about 30meV which can be ascribed to the phonon scattering as discussed below. It means that no well-defined CF excitation was found for the CeOs4Sb12 compound around the expected energy position. This fact contradicts the assumption that CF splitting occurs at 28.2meV for CeOs4Sb12 filled skutterudite proposed in ref. 5 by fitting magnetic susceptibility. On the other hand, the rattling vibration behavior of rareearth ions in a filled skutterudite structure is discussed to be exotic and vital. To further study the inelastic response from CeOs4Sb12, we also performed neutron scattering measurements using LAM-D spectrometer of KEK, in which a final energy of 4.6meV was maintained for outgoing neutrons. Figure 2 shows the spectra of polycrystalline CeOs4Sb12 measured at several temperatures for both the low ( 40 )and high ( 85 )-scattering angle detectors after subtracting the background mainly due to aluminum parts of the sample container and the cryostat. It is clearly seen that the intensity of the spectra increases with increasing temperature at low transfer energies and the intensities at the high scattering angle is higher than those at the low scattering angle, indicating the phonon origin of the spectra. In order to determine the origins of scattering intensities, we divided the obtained spectra by the temperature factor fexpðh !=kBTÞ 1g 1 þ 1, where h ! is the energy transfer, kB the Boltzmann constant and T the temperature. The results are shown in Fig. 3. From Fig. 3 we can see that they decrease weakly with increasing temperature at high energies above 5meV. This indicates that the intensity above 5meV of the spectra reflects the character of phonon excitations. Hence, three clear peaks above 5meV in Fig. 2, i.e., 8, 17 and 25meV for the high scattering angle, and the peak at 17meV for the low scattering angle respectively, result from one-phonon scattering. Similar phonon spectra were found in CeRu4Sb12 at a high scattering angle of 135 for the powder samples. It should be noted that no well-defined CF excitation exists in the finite energytransfer range from the data obtained using the LAM-D -20 0 20 40 60 0.00 0.02 0.04 0.06 0.08