Abstract:Core-shell structured SiC/SiO2 nanowires (SiC/SiO2 NWs) were synthesized by a simple thermal evaporation method without a catalyst. The influence of the growth temperature and holding time on the microstructure and composition of the nanowires were investigated. The results indicate that within the temperature range of 1150 to 1550 degrees C, the color of SiC/SiO2 nanowires gradually transitions from pure white to off-white with increasing temperature. During this process, the average diameter of SiC/SiO2 increases from 74 nm to 291 nm, while the surface SiO2 layer thickness decreases from 17 nm to 5 nm, with nanowires can reach lengths of hundreds of micrometres. Variations in supersaturation of SiO and CO at different temperatures lead to discrepancies in nanowire diameter and SiO2 shell thickness. At 1350 degrees C, prolonged holding time enhances silicon powder reaction, resulting in increased structural disorder of the obtained SiC/SiO2 nanowires. The nanowire growth follows a vapor-solid (V-S) mechanism. Additionally, the study demonstrates that the photoluminescence (PL) characteristics of the nanowires exhibit a blue shift attributable to their nanoscale dimensions, while variations in emission spectra correlate with stacking faults, SiC diameter, and SiO2 thickness. This work may be provide a theoretical basis for preparing SiC/SiO2 nanowires with different diameters and SiO2 shell thicknesses, which is crucial for advancing the development and application of SiC/SiO2 nanoceramics.

Sol-Gel Synthesis And Photoluminescence Of P-Type Semiconductor Cr2o3 Nanowires

Sol-gel Template Synthesis and Photoluminescence of N- and P-Type Semiconductor Oxide Nanowires.

Electroluminescence from Si Nanocrystal/c-Si Heterojunction Light-Emitting Diodes

1.5 Μm Luminescence of Silicon Nanowires Fabricated by Thermal Evaporation of SiO

Room-Temperature Ultraviolet-Emitting In2o3 Nanowires

Catalytic Synthesis and Photoluminescence of Needle-Shaped 3c–sic Nanowires

Sol-gel Synthesis and Photoluminescence of InP Nanocrystals Embedded in Silica Glasses

Catalytic Synthesis and Growth Mechanism of SiC@SiO2 Nanowires and Their Photoluminescence Properties

Triangular prism-shaped p-type 6H-SiC nanowires

Sol–gel Synthesis and Photoluminescence of AlP Nanocrystals Embedded in Silica Glasses

Electronic and Luminescent Properties of Cr-Doped Cadmium Sulfide Nanowires

Growth, structure, and luminescence properties of novel silica nanowires and interconnected nanorings

Luminescence from Colloidal 3C-Sic Nanocrystals in Different Solvents

Fabrication and photoluminescence of bicrystalline SiC nanobelts

Single-crystalline chromium silicide nanowires and their physical properties

A Facile Method for the Fabrication of Luminescent Eu3+-Doped SiO2 Nanowires

Synthesis and Photoluminescence of Single-Crystalline In2O3 Nanowires

Photoluminescence from Er3+ Ion and SnO2 Nanocrystal Co-Doped Silica Thin Films

Synthesis and Room‐Temperature Ultraviolet Photoluminescence Properties of Zirconia Nanowires

Synthesis and electrical properties of ZnO nanowires.

In-situ Synthesis of SiC/SiO2 Nanowires by Catalyst-Free Thermal Evaporation of Silicon Powder and Their Photoluminescence Properties