Observation Of Ferroelectric Domain Patterns In Nanocrystalline Batio3 Ceramics

Xiangyun Deng,Xiaohui Wang,LiangLiang Chen,Hai Wen,Longtu Li

DOI: https://doi.org/10.1063/1.2360244

IF: 4

2006-01-01

Applied Physics Letters

Abstract:Scanning nonlinear dielectric microscopy measurements revealed temperature-dependent variations in contrast, which was attributed to domain rearrangements in 20 nm BaTiO3 ceramics. The experiment result showed the presence of a-c 90 degrees nanoferroelectric domains in 20 nm BaTiO3 ceramics from 25 to 290 degrees C; furthermore the piezoresponse hysteresis loops showed that the 20 nm BaTiO3 ceramics were switchable and ferroelectricity was retained at the high temperature of 290 degrees C, demonstrating the existence of nanoferroelectric domains and the ferroelectric phase still retained above Curie temperature in 20 nm BaTiO3 ceramics, which confirmed the diffused phase transition character in nanograin BaTiO3 ceramics. (c) 2006 American Institute of Physics.