Abstract:Summary form only given. Polycrystalline samples La2/3Caι/3(Mnι_xCox)θ3 with x=0.1, 0.2, 0.3, 0.4, and 0.5 were synthesized by standard solid-state reaction. X-ray diffraction results show that they are of single phase for the specimens with x<;0.3. Rietveld refinement of X-ray diffraction data shows Mn-O-Mn angle decreases from 178.8° for x=0.1 to 128.8° for x=0.3. A metal-to-insulator transition was only observed in sample with x=0.1. The different transport properties of these samples were attributed to the different Jahn-Teller distortion. The temperature dependence of reisitivity at low and high temperature can be described by the small polaron model and Kondo-like effect. In the present work, effect of Co doping at B-site of La2/3Caι/3Mnθ3 (LCMO) is discussed. The spin configuration of Co is very complex. The Co ions are in their low-spin (LS) tg6e2g0 (S=0) state at the low temperature (T<;35 K) and high-spin (HS) tg4e2g2 (S=2) state at high temperature (300 K<;T<;600 K). There maybe a intermediate-spin (IS) tg5e2gl (S=l) state or a mixture of HS and LS of Co3+ in the interval 35 K<;T<;100 K. The structure and properties are close dependent on the Co dopant as discussed below. Polycrystalline samples La,/3Ca2/3(Mnι_xCox)θ3 (LCMCO) with x=0.1, 0.2, 0.3, 0.4, and 0.5 were synthesized by standard solid-state reaction. The analytical purity materials La203, CaC03, Mn02 and Co203 were well mixed in stoichiometric proportions and pestle for 30 minutes before calcined at 1000 °C for 6 hours. The calcined powder was pressed into slices and then sintered at 1400°C for 32 hours in air. All the specimens were slowly-cooled to room temperature in air for about 15 hours. The structure of the samples was characterized by X-ray diffraction (XRD), which was performed at a Rigaku Dmax-γB diffractometer at room temperature with step scanning model. The struct- ral parameters were obtained from a standard Rietveld program GSAS. The resistivity with/without magnetic field were measured by the standard four-probe method at a Quantum Design PPMS. Measurements of x-ray diffraction at room temperature show that samples within x<;0.3 are of single phase which can be well refined in orthorhombic symmetry with the space group of Prima (Rwp<;15%). The lattice parameters of a, b, and c are almost independent of the Co dopant which indicates the unit cell is unchanged after Co was doped in LCMO. The bond angle of Mn-Ol-Mn decreases largely from 178.8° for x=0.1 to 128.8° for x=0.3. It will induce the large change of electric transport properties as discussed below.

Effect Of 6s Lone Pair Of Bi3+ On Electrical Transport Properties Of (La1-Xbix)(0.67)Ca0.33mno3

Effect of Li doping and Li, La co-doping on the structure and physical properties of LaBa2Cu3Oy

Magnetic properties of Bi-doped La0.5Ca0.5MnO3

Effect of Bi doping on the crystal structure, magnetic and magnetocaloric properties of La0.7-Bi Sr0.15Ca0.15MnO3 (x = 0, 0.05, 0.10, 0.15) manganites

Ba2+ doping effect on the charge ordering of Bi0.5Sr0.5−xBaxMnO3 (–0.30)

Ba 2+ doping effect on the charge ordering of Bi 0.5Sr 0.5-xBa xMnO 3 (x = 0 0.30)

Microstructure and Physical Properties of Bi1.9+<i>x</i>Sr1.7−<i>x</i>La0.4CuO6 System

Effect of A-Site Bi-Doping on the Magnetic and Electrical Properties in Tbmno3

Microstructure and Physical Properties of Bi1.9+ x Sr1.7− x La0.4CuO6 System

Effect of Bi3+ Doping on the Electronic Structure and Thermoelectric Properties of (Sr0.889-xLa0.111Bix)TiO2.963: First-Principles Calculations

[Magnetic Properties and Transport Behaviors in Double Doped La(0.67+1.33x)Sr(0.33-1.33x)Mn(1-x)Mg(x)O3 System].

The Effect of Charge Transfer on the Transport and Magnetic Properties Induced by Ca Substitution in La0.3Ce0.2Sr0.5MnO3

Effects of Mn doping on multiferroic and magnetocapacitive properties of 0 . 33 Ba 0 . 70 Ca 0 . 30 TiO 3 – 0 . 67 BiFeO

Effect of Cu Doping on Structure and Physical Properties in the Antiferromagnetic Dirac Semimetal CaMnBi 2

Transport properties in La 0.7− x Gd x Sr 0.3 MnO 3 system

Mixed Doping and Nonstoichiometry Effect in Manganate

Effect of Co doping at the B-site on the structure and tranport properties in La2/3Ca1/3MnO3

The Effect of Ba 2+ Doping on the Structure of SrBi 4 Ti 4 O 15

Effect of A-site average radius and cation disorder on magnetism and electronic properties in manganite La0.6A0.1Sr0.3MnO3\documentclass[12pt]{minimal} \usepackage{amsmath} \usepackage{wasysym} \usepackage{amsfonts} \usepackage{amssymb} \usepackage{amsbsy} \usepackage{mathrsfs} \usepackage{upgreek}

Effect of Mn Doping and Charge Transfer on LaTi1-xMnxO3.

The effect of Cu-doping on the magnetic and transport properties of La 0