Abstract:The tribological behavior of Mo-sprayed piston r ing sliding against grey cast iron cylinder liner under the lubrication of a ful ly formulated petroleum based engine oil SJ/5W-30 containing molybdenum dithioc arbomate (MoDTC) or molybdenum dithiophosphate (MoDTP) was investigated with an Optimol-SRV test rig. The testing temperatures were controlled at 125 ℃ and 32 0 ℃ to simulate the real engine operating conditions.The worn surfaces of the p iston ring and cylinder liner were observed and analyzed by means of scanning el ectron microscopy (SEM) and X-ray photoelectron spectroscopy(XPS). It was obser ved that the frictional behavior of both MoDTC and MoDTP depends heavily on the experimental temperature; MoDTC is effective in decreasing the friction coeffici ent and wear rate at a relatively extended test duration while MoDTP shows frict ion-reduction ability only at relatively high temperatures. It can be seen from the SEM observations of the worn piston ring and cylinder liner surfaces that t he set test temperature range has also strong impact on both the wear severity a nd the wear mechanisms in the contact surface. When it rises from 125 ℃ to 320 ℃, the wear becomes more serious, and the wear mechanism changes from abrasion to adhension. In addition, the chemical interaction between the lubricant conta ining organo-molybdenum and the tribocontact surfaces plays a crucial role in f riction reducing or antiwear film formation, which is dependent on the tribochem ical characteristics of the active ferrous materials and the applied friction mo difiers such as MoDTC or MoDTP. XPS analysis of the worn cylinder liner surfaces indicates that the resultant tribochemical films are mainly composed of iron ox ides, molybdenum oxide, iron sulfide, molybdenum disulfide, and zinc and iron ph osphates. The proportion of these species is a function of both the specific fri ction modifiers used and the experimental temperature. It is supposed that the b etter friction-reduction and wear-resistant actions of MoDTC at 125 ℃ is attr ibuted to the higher content of MoS2 and other wear-resistant compounds gener ated on the worn cylinder liner surfaces.

Tribochemical interactions of piston ring coatings with molybdenum dithiocarbomate friction modifier

Effect of MoDTC and MoDTP on Tribological Behavior of Cylinder Liner/Piston Ring

Effect of Frictional Pair Materials on Tribological Behavior of Molybdenum Dithiocarbomate As an Additive

Tribological Performance of Three Advanced Piston Rings in the Presence of MoDTC-modified GF-3 Oils

Impacts of Molybdenum Dithiocarbamate (modtc) Friction Modifier on Tribological Performance of Fully-Formulated GF-3 Engine Oil

Suppressed MoO3/FeMoO4 formation in molybdenum dialkyl-dithiocarbamate-derived tribofilms on nitrogen-incorporated Al-Mg-Ti-B coatings

Tribological interactions between TiN PVD coating and MoDTC under boundary lubrication conditions

Tribocarbonisation of a Synthetic Engine Oil in Lubricated Piston Ring/cylinder Bore Sliding Contact and Its Relation to Friction and Wear

Tribological Performance of MoS 2 Coating on Slipper Pair in Axial Piston Pump

Tribological performance of MoS2 coating on slipper pair in axial piston pump

Tribological Performance of Magnetron Sputtered Molybdenum Nitride Film on N-Permeated Piston Ring

Tribocatalytic behaviour of a TiO2 atmospheric plasma spray (APS) coating in the presence of the friction modifier MoDTC: a parametric study

Tribological performance of Mn3(PO4)2 coating and PC/MoS2 coating in Rolling–Sliding and pure sliding contacts with gear oil

Influence of Oxidative Degradation of Lubricant and Anti-Friction Modifier on Tribological Behavior of Cylinder Liner/Piston Ring

Synergistic tribological effect between polyisobutylene succinimide-modified molybdenum oxide nanoparticle and zinc dialkyldithiophosphate for reducing friction and wear of diamond-like carbon coating under boundary lubrication

Tribological Performance of Chromium Nitrided Piston Ring Coating

Synergistic Effects of MoDTC and ZDTP on Frictional Behaviour of Tribofilms at the Nanometer Scale

Impacts of Tribochemical Interaction on Lubricating Durability of Engine Oil

Tribological properties of magnetron sputtered MoS2/metal (Ti, Mo) nanocomposite coatings

A study of the tribological properties of Mo-S-Ti composite films prepared by magnetron sputtering

Effect of PAO-4 and MoDTC + ZnDTP oil additive lubricants on the tribological performance of novel tetrahedral amorphous carbon (ta-C) coatings