Abstract:The ability to undercool and solidification mechanism of liquid quinary Ni40Zr28.5Ti16.5Al10Cu5 alloy are investigated by electromagnetic levitation (EML) and drop tube (DT) technique. Under the EML condition, the maximum undercooling of levitated alloy can reach up to 290 K (0.21TL). Under the DT condition, the alloy achieves higher undercooling than EML, and solidifies finally into metallic glass. At lower undercooling, the solidification structure of the alloy is composed of primary Ni3Ti phase, secondary Ni10Zr7 phase and eutectic (Ni10Zr7+Ni21Zr8) phase. With the rise of undercooling, the solidification structure displays the following evolution events: phase morphology refinement, primary phase inhibition, phase number reduction, and amorphous phase formation. By using the high-speed cinematography technique, three nucleation modes are distinctly observed on the levitated alloy melt surface at the beginning of solidification, that is, single-point nucleation, multi-point nucleation and annular nucleation. The levitation state corresponding to single-point mode nucleation is relatively stable, and the alloy undercooling is also relatively low. The annular nucleation only occursin the case with high rotation speed, and the undercooling is greater than 208 K. The discrepancy between nucleation modes is due to the He gas flow for forced cooling. The theoretical calculations indicate that the alloy droplets achieve high undercoolingand large cooling rate under the DT condition. The experimental results show that when the droplet diameter decreases to 498 μm, the amorphous phase begins to appear in the alloy particles. It is noteworthy that the amorphous phase is preferentially formed inside the droplet, but not on the outer surface. The morphology of solidification structure reveals that different regions of the droplet have various local undercoolings, which result in the distribution characteristics of amorphous phase. The volume fraction of amorphous phase increases linearly with the decrease of particle diameter. When the droplet diameter decreases to 275 μm, the alloy droplets are completely frozen into glassy particles. The average eutecticspacing values are also measured at different alloy undercoolings. Compared with the classical binary eutectic growth model, the experimental eutectic growth law exhibits a large deviation in index. This indicates that the eutectic growth in multicomponent alloys displays more complex kinetic characteristics.

Effects of cooling rates on solidification of CuCr25 alloys

The Solidification of Cucr Alloys under Various Cooling Rates

Solidification Microstructure in a Supercooled Binary Alloy

Rapid Solidification Structure Refinement Mechanism in Highly Undercooled Cu Based Ternary Alloys

Effect of cooling rate on microstructure and mechanical properties of rapidly solidified Al-based bulk alloys

Phase Separation of Cu-Pb Monotectic Alloy During Rapid Solidification

Solidification Microstructure Evolution and Grain Refinement Mechanism under High Undercooling of Undercooled Ni90Cu10 Alloys

The Effect of Cooling Rate on the Microstructure Change During Rapid Solidification of Liquid Ti3Al Alloy

Dendritic Growth and Solute Trapping in Rapidly Solidified Cu-based Alloys

Microstructure Refinement Mechanism of Undercooled Cu55Ni45 Alloys

Solidification Pathways of Ternary Cu 62.5 Fe 27.5 Sn 10 Alloy Modulated Through Liquid Undercooling and Containerless Processing

Liquid State Undercoolability and Crystal Growth Kinetics of Ternary Ni-Cu-Sn Alloys

Crystallization Behavior of Fe70Ni10Cr20 During Rapid Solidification under Different Cooling Rates

Rapid Solidification Mechanism of Liquid Quinary Ni-Zr-Ti-Al- Cu Alloy Investigated by High-Speed Cinematography

Effect of Solidification Rates on the Microstructure Morphology of the Cu-Cr Alloy

Effects of cooling rate on the microstructure control and liquid–liquid phase separation behavior of Cu–Fe–P immiscible alloys

Rapid Solidification of Cu60Co30Cr10 Alloy under Different Conditions

Rapid Solidification of Highly Undercooled Ni–Cu Alloys

Simulation Study of the Effets of Various Cooling Rates on Evolution Properties of Micro-Cluster Structure During Solidification Processes of Liquid Metal Cu

Effect of Cooling Rate on Solidification Parameters and Microstructure of Al-7Si-0.3Mg-0.15Fe Alloy

Non-equilibrium Effects on Solid Transition of Solidification Microstructure of Deeply Undercooled Alloys