Abstract:Yttrium is an attractive component for nickel base alloys to improve high-temperature oxidation resistance. However, the application suffers from microstructure related problem, due to less unconscious of Y-related oxidation behavior, especially interacting with other key components, such as aluminium. This study introduces the discovery of microstructure depended external and internal oxidation behaviors based on four simplified Ni-Al-Y alloys during isothermally exposing at 800°C/1000°C in air. Using multiscale microstructural characterizations and thermodynamic calculations, different oxidation layer thicknesses have been observed in the three alloys, especially varying with Y and Al concentrations. In the three high-Y-content alloys, Y-related microstructures are found to strongly drive the oxidation process. Original-Ni5Y compound with strong tendency to precipitate secondary γ-Ni strip is favorable to the formation of inner oxidation layer containing mixed oxide particles, whereas original-γ-Ni phase drives the formation of outer scale of NiO. Dense and well-configured lamella-like phase boundaries (PBs) are beneficial to inhibiting the development of the inner layer, compared to coarse and irregular PBs. The resistance to inner oxidation of minor-Y-addition alloy has been significantly improved at 1000°C, benefiting from the mixed oxides along grain boundaries (GBs) and front of inner oxidation layers. From the thermodynamic basis, a type of modified diagram retrieved from ternary isothermal section is utilized to exhibit the oxide evolution, which is consistent with experimental results, especially for those complicated products.

Oxidation Characteristic of Ignition-Proof Mg-3.5Y-0.8Ca Alloys at High Temperatures

Characteristics of oxidation film on ignition-proof Mg-3.5Y-0.8Ca alloys at high temperatures

Selective Oxidation Behavior of an Ignition-Proof Mg-Y-Ca-Ce Alloy

Oxidation Behavior of Ignition-Proof Magnesium Alloys with Rare Earth Addition

Oxidation Mechanism of Three Fe-Al Alloys with and Without Addition of 0.1 At% Yttrium at 800 °C

Effect of Ca and Y Additions on Oxidation Behavior of AZ91 Alloy at Elevated Temperatures

Early oxidation behaviors of Mg–Y alloys at high temperatures

Oxidation Resistance of Mg-Xca (X=0.3, 1.0, 2.0 and 3.6 Wt.%) Alloys in Flame

Study on oxidation kinetics of ignition-proof magnesium alloys with rare earth addition

Flame resistance and oxidation behaviour of Mg–xCa (x=0.3, 1.0, 2.0 and 3.6 wt.%) alloys

The high-temperature oxidation resistance properties of magnesium alloys alloyed with Gd and Ca

Early high temperature oxidation behaviors of Mg–10Gd–3Y alloys

Flame Ignition Mechanism of Magnesium Alloys Controlled by Oxide Films Based on the Oxidation Behaviors of Al, Nd and Y

Micro-arc Oxidation Behaviors of AZ91D Magnesium Alloy in Different Electrolytes

Raising the Oxidation Resistance of Low-Alloyed Mg-Ca Alloys Through a Preheating Treatment in an Argon Atmosphere

In-mold Oxidation Behavior of Mg–4.32Y–2.83Nd–0.41Zr Alloy

Research and Development of New Style Ignition-proof Magnesium Alloys

Influence of calcium on ignition-proof mechanism of AM50 magnesium alloy

Effect of Ca addition on the oxidation resistance of AZ91 magnesium alloys at elevated temperatures

Effect of Y on oxide film formation and ignition behavior of magnesium-rare earth alloy

Unveiling the mechanism of yttrium-related microstructure inhibiting or promoting high-temperature oxidation based on Ni-Al-Y alloys