Abstract:The thermodynamic stability of intermetallic compounds formed by most conventional alloying elements in Mg alloys is not high, resulting in the poor heat resistance of Mg alloys. Although rare earth (RE) compounds have superior thermal stability, the melting point of Al-RE compounds is generally higher than that of Mg-RE compounds. Therefore, in-depth exploration of the influence mechanism of RE compounds on the heat resistance of Al-containing Mg alloys is necessary. In this work, the thermodynamic stability of the might exist precipitates in Mg–Al–Zn–Mn–Y alloys was analyzed using first-principles calculations and verified via scanning electron microscope (SEM), X-ray diffraction (XRD), energy dispersive spectrometer (EDS), and other experimental methods. Based on their results, the precipitation sequence of the key RE precipitates was deduced. Furthermore, it was investigated whether the preferentially precipitated precipitates could serve as the nuclei of primary α-Mg based on the mismatch theory. Consequently, the refinement mechanism of Y on Mg alloys was elucidated. Besides, the complex alloying reactions in the multi-elemental Mg alloy system were simplified using the electronegativity theory and the Al–Y, Mg–Y, Mg–Al binary phase diagrams, and the strengthening mechanism of Y on Mg alloys was elucidated eventually. The results indicated that the preferentially precipitated granular Al8Mn4Y and Al2Y prevented Mg17Al12 from forming a network structure, and a reinforced structure was formed in which the modified Mg17Al12 particles were mixed with the newly formed granular Al8Mn4Y and Al2Y. Tensile tests and fracture analyses indicated that the reinforced structure improved the mechanical properties of the alloy both at room and elevated temperatures.

Oxidation Behavior of Ignition-Proof Magnesium Alloys with Rare Earth Addition

Oxidation Mechanism of Three Fe-Al Alloys with and Without Addition of 0.1 At% Yttrium at 800 °C

Micro-arc Oxidation Behaviors of AZ91D Magnesium Alloy in Different Electrolytes

Research Progress on the Oxidation Behavior of Ignition-Proof Magnesium Alloy and Its Effect on Flame Retardancy with Multi-Element Rare Earth Additions: A Review

In-mold Oxidation Behavior of Mg–4.32Y–2.83Nd–0.41Zr Alloy

Oxidation Resistance of Mg-Xca (X=0.3, 1.0, 2.0 and 3.6 Wt.%) Alloys in Flame

Flame resistance and oxidation behaviour of Mg–xCa (x=0.3, 1.0, 2.0 and 3.6 wt.%) alloys

The high-temperature oxidation resistance properties of magnesium alloys alloyed with Gd and Ca

Raising the Oxidation Resistance of Low-Alloyed Mg-Ca Alloys Through a Preheating Treatment in an Argon Atmosphere

The oxidation behavior of Mg-Er binary alloys at 500 °C

Experiments on Oxidation and Combustion Behaviors of Cerium Metal Slice with Slow Heating under O2/Ar Atmospheric Conditions

Microstructure and Mechanical Properties of Mg-Xy-1.5mm-0.4zr Alloys

Study on the strengthening mechanism of rare earth yttrium on magnesium alloys

Oxidation behavior and improvement in nonflammability of LPSO-type Mg–Zn–Y–Sr alloy

Post-fire residual service performance of magnesium alloys reinforced by rare earths

Oxidation and Ignition Behaviors of Molten Mg-Nd-Zr Alloy in Resin-Sand Mold

Study on the Strengthening Mechanism of Rare Earth Ce in Magnesium Alloys, Based on First-Principle Calculations and Electronegativity Theory

Influence of calcium on ignition-proof mechanism of AM50 magnesium alloy

Oxidation Behavior of Molten Magnesium in Atmospheres Containing SO2 and Air in a Sealed Furnace

Study on Micro-arc Oxidation of Mg-Zn-Y-Nd-Ca Magnesium Alloys

Effects of Al, Zn, and rare earth elements on flammability of magnesium alloys subjected to sonic burner–generated flame by Federal Aviation Administration standards