Effect of Aging Temperature on Erosion-corrosion of 17-4PH Casting Stainless Steels in Dilute Sulfuric Acid Slurry

LI Ping,CAI Qi-zhou,WEI Bo-kang,ZHANG Xian-zhong
DOI: https://doi.org/10.3321/j.issn:1004-0595.2006.04.011
2006-01-01
Tribology
Abstract:Effect of aging temperature on erosion-corrosion of precipitation-hardened 17-4 PH casting stainless steel in 0.01mol/L dilute sulfuric acid slurry containing silica particles was studied by using a home-made slurry pot device.Microstructure was observed with optical microscope and transmission electron microscope(TEM),influence of impact velocity on erosioncorrosion of 17-4PH steels at different aging temperature was also analyzed,the morphologies of the worn surfaces of the samples after erosion-corrosion was observed using a scanning electron microscope(SEM),and erosion-corrosion wear mechanisms were discussed based on the morphologies of the worn surfaces.Results show that with the same solution heat treatment,hardness reaches the maximum value near 460 ℃.Erosion-corrosion for 17-4PH stainless steels at different aging temperature showes that pure erosion-wear is dominating,corrosion is subordinate,and at the same time corrosion promotes wear.Influence of aging treatment temperature on erosion-corrosion rate of 17-4PH steels is not significant under lower impingement velocity,but under higher impingement velocity the erosion-corrosion resistance of 17-4PH steels aged near 460 ℃ reaches maximum due to precipitation strengthening effect of fine and dispersed e-Cu phase. With a prerequisite of appropriate corrosion resistance the precipitation hardening could improve significantly the erosion corrosion property of the materials.
What problem does this paper attempt to address?