Abstract:The corrosion mechanism and characteristics of steel in typical atmospheric environments directly affect the rationality of corrosion protection methods. This study investigates the corrosion evolution law of Q235 steel that has been exposed to the urban industrial atmosphere for seven years. The mass loss is used for corrosion dynamics analysis. The rust layers have been characterized by SEM, EDS, and XRD. Finally, the corrosion mechanism was analyzed through a combination of electrochemical methods, corrosion kinetics, and rust layer characteristics. The mass loss results indicate that a two-stage corrosion power function law can still effectively describe the corrosion rate of a seven-year exposure that complies with the power function law. The short-term corrosion results fail to fully reflect the corrosion performance of Q235 steel. The typical morphological structures of γ-FeOOH and α-FeOOH are identified, and the rust layers change from a loose and flat form to a granular and, finally, compact into a smooth surface. The crystalline phases of the rust layers include α-FeOOH, γ-FeOOH, Fe3O4/γ-Fe2O3 and α-Fe2O3. Corrosion products in the initial period are mainly γ-FeOOH, followed by α-FeOOH, and a small amount of Fe3O4/γ-Fe2O3. With the increase in exposure time, α-FeOOH and Fe3O4/γ-Fe2O3 in the rust layer increase. SO2 and Fe3O4/γ-Fe2O3 are the primary factors accelerating steel corrosion. During the first three years of atmospheric corrosion, the primary corrosion mechanism was governed by the acid cycle reaction mechanism. However, from the fifth year of atmospheric corrosion, oxygen-absorbing corrosion began to gradually dominate, specifically oxygen-absorbing corrosion.

PROGRESS IN RESEARCH ON RUST LAYER OF WEATHERING STEEL

The Evolution of the Corrosion Mechanism of Structural Steel Exposed to the Urban Industrial Atmosphere for Seven Years

Insights into the Corrosion Mechanism and Electrochemical Properties of the Rust Layer Evolution for Weathering Steel with Various Cl− Deposition in the Simulated Atmosphere

Influence of Carbon Content on Corrosion Resistance Performance of Weathering Steel

Roles of grain refinement in the rust formation and corrosion resistance of weathering steels

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

Optimizing the corrosion performance of rust layers: role of Al and Mn in lightweight weathering steel

The Role of the Direct Current Electric Field in Enhancing the Protective Rust Layer of Weathering Steel

Corrosion behavior of weathering steel in marine atmosphere

Corrosion Micro- and Macro-Electrochemical Behavior of Rusted Carbon Steel and Weathering Steel

ANALYSES OF FORMATION OF WHITE RUST ON HOT DIP GALVANIZED STEEL AND RELEVANT COUNTERMEASURES

Study on corrosion performance and corrosion product composition of weathering steel and high‐performance steel in simulated C3 environment

Effect of rust layer stabilization on dry and wet cyclic corrosion behavior of bridge weathering steel Q345qNH in simulated industrial atmospheric medium

Study of effects of rare earth elements on the corrosion behavior of weathering steels under a simulated immersion environment and a real atmospheric environment

Introduction to Atmospheric Corrosion Research in China

A Study on the Weatherability of Weathering Steel after Atmospheric Corrosion

Corrosion Resistance Performance of Molybdenum-Containing Weathering Steel

The improvement of weathering resistance by increasing P contents in cast strips of low carbon steels

On how the corrosion behavior and the functions of Cu, Ni and Mo of the weathering steel in environments with different NaCl concentrations

Study on performance evaluation and maintenance management system of weathering steel bridge

Corrosion behavior of the low alloy weathering steels coupled with stainless steel in simulated open atmosphere