Influence of Adding Al on the Microstructure and Mechanical Properties of C/C-SiC Composites Fabricated by MSI

RAN Liping,YI Maozhong,WANG Chaosheng,PENG Ke,HUANG Boyun

DOI: https://doi.org/10.3321/j.issn:1000-3851.2006.05.007

2006-01-01

Abstract:C/C-SiC composites were fabricated by molten silicon infiltration(MSI) to C/C preforms prepared by chemical vapor infiltration(CVI).The influences of adding Al in molten Si infiltrating agent on the microstructure and mechanical properties of the composites was studied.The results show that the composites fabricated by infiltrat-ing Si into C/C preforms contain SiC,C and residual Si phases.With the increasing of the amount of adding Al in the agent,the amount of Al phase in the composites increases and the amounts of other phases such as SiC and Si phase decrease.SiC phase distributes around the carbon fiber,and Si phase exists far away from the carbon fiber where there is nearly no Al phase.The bending strength and the fracture toughness increase with the increase of the amount of adding Al.When the amount of Al increases from 0 to 10%,the bending strength increases from 116.7MPa to 175.4MPa and the fracture toughness from 5.8MPa·m~(1/2)to 8.6MPa·m~(1/2),that is,by 50.3% and 48.2% respectively.The Al phase makes the fracture mechanism of the composite become toughness fracture.