Synthesis and Characterization of the Mixed Mg/Al Hydrotalcite‐Like Compounds
Shu-Ping Li,Zhi-Ping Zhou
DOI: https://doi.org/10.1080/01932690600856883
2006-01-01
Journal of Dispersion Science and Technology
Abstract:A series of mixed MgAl-HTlc, Mg1-xAlx-NO3-HTlc (where X=M(III)/(M(III)+ M(II))=1/3 in the starting solution) were prepared following the coprecipitation method at a constant pH under different synthesis temperatures. Their structural, textual and rheological properties were examined respectively. It is found from the results that the increase of the synthesis temperature will increase the interlayer spacing of the layered compounds, but under the room temperature, the sample shows the best crystallinity. Nitrogen adsorption isotherms were used to determine the surface areas and pore structure of these compounds, and the effect of the synthesis temperature on the surface characteristics is discussed. It is thought that the microporosity was related to the treatment temperature, and most of the samples contain large amount of micropores about 1.5 nm. The results of the hydrated diameters showed that all the samples are polydispersity, but flocculation occurred in the samples, which were prepared under higher temperatures. The flow curve of the suspension showed that the samples, which were prepared under relatively low temperatures, behaved as Newton-like behavior with a slight shear-thickening, whereas the flow curves of the other samples, which were prepared under higher temperatures, are shear-thinning, typical behavior of the flocculated system. The result of the rheology is accordant with the results of the hydrated diameters, the coagulation suspension showed the non-Newton flow behavior, whereas the other suspensions showed the Newton-like flow.