Effect Of Sm3+ And Co2+ Doping Into Znfe2o4 Nano-Ferrite On Electromagnetic Loss Property

J Zhuang,Xp Chen,Yh Chi,Dm Yang
DOI: https://doi.org/10.3321/j.issn:0567-7351.2006.02.009
2006-01-01
Acta Chimica Sinica
Abstract:The precursors of basic carbonates and ferric hydrate for ferrite were prepared by solid-state reaction at room temperature and characterized by TG-DSC. The nanometer spinel ferrites with the average size of 62 nm were obtained by microwave heating at 600 W for 10 min, then thermolysis at 550 C, and studied by a laser granularity analyzer, XRD and SEM. The electromagnetic loss property was studied by the relative dielectric constant and relative magnetic permeability of the ferrites. The results show that when Co2+ partially substituted Zn2+ in ZnFe2O4, the electromagnetic loss property of materials was obviously improved in 100 similar to 1800 MHz. On the other hand when Fe3+ was substituted less by Sm3+ in Co0.5Zn0.5Fe2O4, the electromagnetic loss property of materials was increased properly.
What problem does this paper attempt to address?