Abstract:In this paper, we have investigated in detail the preparation of anatase TiO2 catalysts by the controlled thermal decomposition of ammonium titanyl sulfate ((NH4)(2)TiO(SO4)(2)) and their catalytic activity. The structures of anatase TiO2 catalysts have been characterized by powder X-ray diffraction, N-2 adsorption-desorption isotherms, diffuse reflectance UV-vis spectroscopy, infrared spectroscopy, X-ray photoemission spectroscopy, NH3 temperature-programmed desorption, and solid-state MAS NMR spectrometer. We report for the first time that the anatase TiO2 catalyst prepared by calcination of (NH4)2TiO(SO4)2 at 600 degrees C (TiO2-600) is a very active bifunctional catalyst. TiO2-600 is doped with N and S and thus very active in the photodegradation of methyl orange under visible light illumination (lambda > 420 nm); meanwhile, it also has a large number of Bronsted acid sites arising from the covalently bonded sulfuric acid groups and thus is active in the esterification of ethanol and acetic acid to ethyl acetate. The Pt/TiO2-600 photocatalysts with different Pt loadings were prepared via the incipient wetness impregnation method and their photocatalytic activity for the H-2 production from water splitting was evaluated with methanol as a sacrificial electron donor under both all-wavelength light and visible light (lambda > 400 nm) irradiation. All Pt/TiO2-600 photocatalysts show considerable photocatalytic activity of water splitting. The optimum Pt loading on TiO2-600 is 1 and 0.1 wt % for the all-wavelength light and visible light photocatalytic reaction, respectively. Our results demonstrate a facile method to prepare highly active bifunctional TiO2 catalysts promising in both visible-light-driven photocatalysis and acid catalysis.

Preparation And Characterization Of Visible-Light Responsive Photocatalyst S/Tio2

Preparation of WO<sub>x</sub>-TiO<sub>2</sub> and the Photocatalytic Activity under Visible Irradiation

A Visible Light-Driven Titanium Dioxide Photocatalyst Codoped with Lanthanum and Iodine: an Application in the Degradation of Oxalic Acid

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

One-Step Synthesis Of Bifunctional Tio2 Catalysts And Their Photocatalytic Activity

Synthesis and Photocatalysis Properties of Sulfur Doped Nanocrystalline TiO2 Photocatalyst

Preparation and Characterization of Visible-Light-active Nitrogen-Doped TiO2 Photocatalyst.

Preparation, Characterization, and Photocatalytic Activity of Visible Light Driven Chlorine-Doped Tio2

One-step synthesis of highly active Ti-containing Cr-modified MCM-48 mesoporous material and the photocatalytic performance for decomposition of H 2S under visible light

Simple fabrication and photocatalytic activity of S-doped TiO2 under low power LED visible light irradiation

Preparation of AgI Sensitized Amorphous TiO2 As Novel High-Performance Photocatalyst for Environmental Applications

Preparation of Magnetically Supported Chromium and Sulfur Co-Doped TiO2 and Use for Photocatalysis under Visible Light

Preparation And Properties Of The Copper Phthalocyanine Tetrasulfonate Sensitized Tio2 Photocatalyst

Fabrication of Nitrogen and Sulfur Codoped Titanium Dioxide and Its Visible Light Photocatalytic Activity

Characterization and Visible-Light-Activity of Nitrogen-Doped Tio2 Photocatalyst

Synthesis, Characterization, and Photocatalytic Properties of Sulfur- and Carbon-Codoped TiO2 Nanoparticles

Processing Tio2 in Gaseous Sulfur and Research on Its Photocatalysis under Visible Light

Preparation of Solid Superacid SO2-4/TiO2 and Evaluation of Their Photocatalytic Oxidation Activity

Preparation and Properties Characterization of Visible-light-driven N-doped TiO2

Preparation of solid superacid SO4 2-/TiO2 and evaluation of their photocatalytic oxidation activity

Preparation of a solid superacid catalyst SO_4~(2-) /TiO_2 and its photocatalytic oxidation activity