Synthesis Of Nd:Ggg Powder By Liquid Phase Co-Precipitation Or Solid State Method And Preparation Of Its Transparent Ceramic
Zhang Xuejian,Li Chun,Huang Dexin,Lu Zhuofei,Zhang Ying,Liu Jinghe
DOI: https://doi.org/10.4028/www.scientific.net/AMM.651-653.119
2014-01-01
Applied Mechanics and Materials
Abstract:Neodymium-doped gadolinium gallium garnet (Nd:GGG) precursor and ceramic were prepared by liquid phase co-precipitation or solid-state methods, and the properties were studied. The results indicate that the precursor prepared with the liquid phase co-precipitation method has a small particle size. The sub-transparent ceramic was obtained after the body sintered for 2-3h at 1650 degrees C at 1100Pa using liquid-phase co-precipitation method. When the body was sintered at 1750 degrees C for 2-3h, a sintered body with non-transparency was obtained. The absorption spectrum and fluorescence spectrum of the sub-transparent ceramic were measured with the cross section at 807nm was calculated as1x10-(20) cm(2) and the strongest emission peak located at 1061nm.Neodimium doped Gadolinium gallium Garnet crystal, which is a comprehensively used laser material, possesses unique laser properties, such as high mechanical strength and thermal conductivity compared with Nd doped glasses. Recently, lots of achievements have been abtained in areas of ceramic laser matrix, which plays a very important role in solid state high power laser field. High quality and large size Nd: GGG crystal is hard to prepare at present [1]. So, preparation of Nd: GGG transparent ceramic offers a new thinking in finding excellent laser materials.Excellent quality Nd: GGG nanopowder must be prepared before transparent ceramic. Solid State method, Liquid Phase Co-precipitation, Sol-gel method and hydrothermal method are main powder process methods at present. Nd: GGG nanopowder were prepared by Solid state method and Liquid phase co-precipitaion method, respectively. The samples were molding and sintering process were compared([2-7]).