Abstract:Phenolic resins occupy an important position in industrial applications, but phenol, one of the raw materials for synthesis, is a non-renewable resource. Lignin, as a natural polymer containing phenolic hydroxyl groups, alcohol hydroxyl groups and other reactive groups, can replace some of the phenol in the synthesis of phenolic resins, which can reduce the amount of phenol, thus reducing the cost of phenolic resins, while effectively promoting the high value-added use of renewable biomass resources. Due to its low reactivity, alkaline lignin is usually discharged as production waste, unaware that lignin macromolecules can be modified. In this paper, the phenolic monomers were obtained by acid-catalyzed depolymerization of DES (choline chloride/p-toluenesulfonic acid or choline chloride/lactic acid) from waste alkaline lignin, and the recovery rate of the DES solution during the catalytic treatment was more than 85 %, in which the main monomer was 2-methoxy-4-(1-propyl) phenol. The degradation of alkaline lignin is still favorable after five times of DES solvent recovery. The depolymerized lignin monomer replaced phenol by 50 wt% and then ternary co-polymerized with phenol and formaldehyde to form a biomass phenol-based phenolic resin, providing a green route for phenolic resin production. The cost of resin preparation was economically calculated, and it was found that the cost of resin after accumulating 4 cycles of DES treatment was only 51.1 % of that of pure phenolic resin. The density functional theory (DFT) was used to simulate the possible radical reactions in the intermediate process of phenolic resin reaction, to explore the microscopic mechanism and competition, to provide theoretical reference for further experimental realization of resin structure control and optimization, and to improve the theoretical system of resin synthesis.

Structural investigation of phenolic resin through 1H-NMR analysis

Structure-property Relationships for Technical Lignins for the Production of Lignin-Phenol-formaldehyde Resins

New Insights into High-Ortho Phenolic Novolac: Elucidating Dependence Between Molecular Structure, Curing Kinetics and Thermal Stability

The Structure Analysis and Characterization of N-100 by Nmr

Structure–properties relationship for resols with different formaldehyde/phenol molar ratio

A study of phenolic aldehyde resins by pyrolysis gas chromatography mass spectrometry

Use Of Hydroxymethylated Lignin In Phenol-Formaldehyde Resins

Preparation and Characterization of Phenol-Formaldehyde Resins Modified with Alkaline Rice Straw Lignin

Structural Evolution of Phenolic Fibers during the Forming Process

Reactivity and Property of Phenolic Resin Synthesized by Phenol and Paraformaldehyde

Structural Description of Polyaromatic Nucleus in Residue

Density Functional Theory Study on Thermal Cracking Reaction Mechanism of Phenolic Resin

Elucidating the chemical structures of petroleum resin using solid-state 13C NMR

Characterization of Alkaline Lignins for Use in Phenol-Formaldehyde and Epoxy Resins

Synthesis and Structure Characterization of Boron-Nitrogen Containing Phenol Formaldehyde Resin

A novel thermal degradation mechanism of phenol–formaldehyde type resins

Separation and characterization of alkyl phenol formaldehyde resins demulsifier by adsorption chromatography, gel permeation chromatography, infrared spectrometry and nuclear magnetic resonance spectroscopy

Preparation of high molecular weight thermoplastic bio-based phenolic resin and fiber based on lignin liquefaction

Hydroxymethylation of softwood kraft lignin and phenol with paraformaldehyde

Behavior Investigation of Phenolic Hydroxyl Groups During the Pyrolysis of Cured Phenolic Resin Via Molecular Dynamics Simulation

Characterization and properties of phenolic resin doped modified lignin