Abstract:The Ni0.5Zn0.5Fe2O4/SiO2 composite nanofibers were prepared using sol-gel process combined with electrospinning. The thermal decomposition and phase inversion process of precursor nanofibers and the effects of calcination temperature and SiO2 content on the phase composition, microstructure, morphology and magnetic property of the resulting nanofibers were studied by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, high resolution transmission electron microscopy and vibrating sample magnetometer. The experimental results show that the cubic spinel structure is basically formed when the precursor nanofibers are calcined at 450 ℃ for 2 h. The average grain size of Ni0.5Zn0.5Fe2O4 contained in the composite nanofibers with 10 % SiO2 and their specific saturation magnetization and coercivity increase with increasing calcination temperature. Amorphous SiO2 additive can effectively restrain the growth of Ni0.5Zn0.5Fe2O4 nanocrystals. As a result, with SiO2 content increasing from 0 to 20 % , the average grain size of Ni0.5Zn0.5Fe2O4 in the prepared Ni0.5Zn0.5Fe2O4/SiO2 composite nanofibers calcined at 900 ℃ for 2 h decreases from 81.6 to 13.3 nm, and the specific saturation magnetization of these samples monotonically decreases, whereas the coercivity initially increases and then decreases due to the change of magnetic domain structure from multi-domain to single-domain along with the reduction in grain size. In addition, with the increase of SiO2 content, the diameter of the as-prepared Ni0.5Zn0.5Fe2O4/SiO2 composite nanofibers gradually increases and the surface becomes smooth.

Preparation Of Magnetic Composite Of Nife2o4@Sio2 And The Assembly Of The Colloid Particles By Magnetic Fields

PREPARATION OF MAGNETIC COMPOSITE OF <font>NiFe</font><sub>2</sub><font>O</font><sub>4</sub><font>@SiO</font><sub>2</sub> AND THE ASSEMBLY OF THE COLLOID PARTICLES BY MAGNETIC FIELDS

Preparation of Magnetic Fe3O4/SiO2 Nano-composite Particles by Chemical Deposition in Aqueous Solution

Synthesis and Magnetic Properties of Nearly Monodisperse CoFe2O4Nanoparticles Through a Simple Hydrothermal Condition.

Preparation and Characterization of Nano-magnetic Fe3O4-SiO2 Composite

Preparation of One-Dimensional Ni0.5 Zn0.5 Fe2O4/SiO2 Composite Nanostructures and Their Magnetic Properties

The Effect of Surface Modification on the Morphology and Magnetic Properties of Nife2o4 Nanoparticles

Preparation and Characterization of Nife2o4/Nio Composite Film Via A Single-Source Precursor Route

Preparation and Surface Modification of Fe<sub>3</sub>O<sub>4 &Lt;/sub>nano-Magnetic Powders

Preparation and Magnetic Properties of Doped Ni-Fe/Fe3O4 Nanocomposite

Preparation,structure and Magnetic Properties of Silica/mefe2o4 Hollow Composite Spheres

Synthesis and magnetic properties of iron/silica core/shell nanostructures

Facile Synthesis and Magnetic Properties of Monodisperse Fe3O4/silica Nanocomposite Microspheres with Embedded Structures Via a Direct Solution-Based Route

Preparation and characterization of γ-Fe_2O_3/SiO_2 magnetic nanocomposites

In Situ Dispersion of Non-Aqueous Fe3O4 Nanocolloids by Microdroplet Coalescence and Their Use in the Preparation of Magnetic Composite Particles.

Preparation of High Magnetic Fe_3O_4/TiO_2 Composite Particles

Preparation of SiO2/Ni core-shell structured nanoparticles and their magnetic properties

Preparation of Core Shell Particles Consisting of Cobalt Ferrite and Silica by Sol–gel Process

Preparation of Porous SiO2/Ni/TiO2 Multicoated Microspheres Responsive to Electric and Magnetic Fields

Preparation and magnetic properties of doped Ni-Fe/Fe3O 4 nanocomposite

Preparation and characterization of narrow-dispersed magnetic colloidal nanoparticle cluster/silica microspheres with controlled sizes, high saturation magnetization and MRI enhancement effect