Abstract:Highly ordered TiO2 nanotube arrays were fabricated by electrochemical anodization of titanium in an NH4F/H3PO4 electrolyte. A TiO2 crystal phase was identified by X-ray diffraction, and the morphology, length and pore diameter of the TiO2 nanotube arrays were determined by field-emission scanning electron microscopy (FE-SEM). The anodization parameters including the rate of magnetic stirring, F− concentration, calcination temperature, anodization voltage and anodization time were investigated in detail. The results show that the as-prepared TiO2 nanotube arrays possessed good uniformity, a well-aligned morphology with a length of 750nm and an average pore diameter of 62nm at a 150rpm rate of magnetic stirring for 120min at 20V in an electrolyte mixture of 0.2M H3PO4 and 0.3M NH4F with a 500°C calcination to obtain 100% anatase phase. The adsorption of N-719 dye at different tube lengths was determined by UV-vis analysis and found to increase with increasing tube length. We also discuss the formation mechanism of the TiO2 nanotube arrays. The findings indicate that the formation of the TiO2 nanotube arrays proceeds by the combined action of the electrochemical etching and chemical dissolution.

In Situ Templated Synthesis of Anatase Single-Crystal Nanotube Arrays.

Rapid-Heating-Triggered in Situ Solid-State Transformation of Amorphous TiO2 Nanotubes into Well-Defined Anatase Nanocrystals

Controlled Synthesis of Anatase Tio2 Nanotube and Nanowire Arrays Via Aao Template-Based Hydrolysis

In Situ Template Synthesis of TiO<sub>2</sub> Nanotube Array Films

In-situ template synthesis of TiO2 nanotube array films

Synthesis of Highly-Ordered Tio2 Nanotube Arrays with Tunable Sizes

In-situ template synthesis of TiO2 nanotube array films on Al substrates

In-Situ Template Synthesis Titania Nanotube Array Films on Aluminum Plate

Crystal phase transition and properties of titanium oxide nanotube arrays prepared by anodization

Fabrication of TiO2 Nanotube Arrays by Electrochemical Anodization in an NH4F/H3PO4 Electrolyte

Template-based Synthesis and Micro-structure Characterization of TiO2 Nano-array

Low-Temperature Synthesis of High-Ordered Anatase Tio2 Nanotube Array Films Coated with Exposed {001} Nanofacets

Controlling the Synthetic Pathways of Tio2-Derived Nanostructured Materials

Electrochemically Induced Sol-Gel Preparation of Single-Crystalline Tio2 Nanowires

Array of Single Crystalline Anatase TiO2 Nanotubes with Significant Enhancement of Photoresponse

In Situ Synthesis and Characterization of TiO 2 Nanoarray Films

In-situ evolution of anodic TiO2 nanotubes to ammonium oxofluorotitanate mesocrystals and their conversion to mesocrystalline TiO2

Selective Synthesis of TiO2 Single Nanocrystals and Titanate Nanotubes: a Controllable Atomic Arrangement Approach Via NH4TiOF3 Mesocrystals.

Fabrication of open-ended TiO2 nanotube arrays by anodizing a thermally evaporated Ti/Au bilayer film

Templated Synthesis of TiO2 Nanotube Macrostructures and Their Photocatalytic Properties

Synthesis of Thin Films of Barium Titanate and Barium Strontium Titanate Nanotubes on Titanium Substrates