Abstract:Traditional laser processing technique is mainly applied for cardiovascular stent manufacture, especially for materials with high mechanical properties and high melting point, while it usually produces problems such as material ablation and defects during finish machining process. Magnesium alloy, as material candidate for bioresorbable cardiovascular stent, has low melting and ignition point, high oxidizability property. Laser processing technique scarcely meets the requirements of high surface quality of magnesium alloy cardiovascular stents, this paper firstly develops a five-axis micro-milling technique to fabricate magnesium alloy cardiovascular stents. Milling orthogonal test was carried out to obtain the optimal finish machining parameters, and then a novel stent machining process was established. The processed stent has an inner diameter of 1.5 mm, a thickness of 80 & mu;m and a length of 8 mm with a U-bend width of 100 & mu;m and a link strut width of 70 & mu;m, and the optimal finish processing parameters was set up with the main spindle speed of 30,000 rpm, feed speed 200 mm/min, cutting width 50 & mu;m and cutting depth 40 & mu;m. The dimensional accuracy and surface topography of the magnesium alloy stent were measured and characterized, and results showed that the dimensional accuracy was within 0.01 mm, and the machined stent achieved better surface quality without obvious processing defects such as pits, grooves and pores while comparing with the stent under original processing parameters. In order to evaluate the radial support performance of the stent, the radial compression and expansion experiments and simulations were conducted, respectively. Results showed that the maximum diameter error in the experiment and simulation was 13.35 %, and the radial recoiling error was 16.79 %. This work provides a potential stent manufacture technique in the development and clinical application of bioresorbable magnesium alloy stent.

Design and fabrication of coronary stent

The fabrication of micro-hole stent by laser cutting

Computational biomechanics and experimental verification of vascular stent

Laser micro-processing of cardiovascular stent with fiber laser cutting system

Fiber Laser Cutting Technology on Coronary Artery Stent

High-Performance Self-Expanding NiTi Stents Manufactured by Laser Powder Bed Fusion

A Survey of Coronary Stents Development

Cardiovascular stent cutting technique by fiber laser

Experimental research on laser interference micro/nano fabrication of hydrophobic modification of stent surface

Investigation on Fiber Laser Micromachining and Mechanical Performances of Endovascular Stent

Electrochemical polishing, characterisation and in vitro evaluation of additively manufactured CoCr stents with personalised designs

Finite Element Simulation and Experimental Verification of Laser Machining of Nitinol Tubes

The Development of Design and Manufacture Techniques for Bioresorbable Coronary Artery Stents

The Process and Performance of Endovascular Stents

Finite Element Analysis on the Crimped Mechanical Behavior of Coronary Stents

Mitigation of bio-corrosion characteristics of coronary artery stent by optimising fs-laser micromachining parameters

Fabrication of Hydrophobic Structures on Coronary Stent Surface Based on Direct Three-Beam Laser Interference Lithography

Laser Processing Technology and Its Research Progress of Vascular Stent

Study on Surface Quality and Mechanical Properties of Micro-Milling WE43 Magnesium Alloy Cardiovascular Stent

3D Printing and Characterization of the Biodegradable Vascular Stent

Improve Endothelialization of Metallic Cardiovascular Stent Via Femtosecond Laser Induced Micro/nanostructure Dependent Cells Proliferation and Drug Delivery Control