Novel sulfonated N-heterocyclic poly(aryl ether ketone ketone)s with pendant phenyl groups for proton exchange membrane performing enhanced oxidative stability and excellent fuel cell properties
Qian Liu,Xiaoke Li,Shouhai Zhang,Zhaoqi Wang,Yuning Chen,Shengyang Zhou,Chenghao Wang,Kaiwen Wu,Jianguo Liu,Qing Mao,Xigao Jian
DOI: https://doi.org/10.1016/j.memsci.2021.119926
IF: 9.5
2022-01-01
Journal of Membrane Science
Abstract:Novel sulfonated poly(bis-phthalazinone ether ketone ketone)s containing pendant phenyl moieties (SP-BNPs) are prepared from poly (bis-phthalazinone ether ketone ketone)s containing pendant phenyl groups via post-sulfonated modification. The resulting polymers possess the ion exchange capacity ranging from 0.91 to 1.46 mmol g-1 and intrinsic viscosity scattering from 3.9 to 6.4 dL g-1. SP-BNPs membranes are manufactured using the solution-casting method with water absorption up to 17.1%. The swelling rate of SP-BNPs membranes is up to 5.6%, and the tensile strength is higher than 62 MPa. The proton conductivity ranges from 9.8 to 103 mS cm-1 at 75 °C. The breaking time of SP-BNPs membranes in Fenton's reagent at 80 °C is longer than 3 h. The result indicates that SP-BNPs membranes exhibit better oxidation stability than sulfonated poly(ether ether ketone)s and sulfonated poly(phthalazinone ether ketone) membranes. The peak power density of the cells equipped with SP-BNPs membranes is up to 1790 mW cm-2. The introduction of phthalazinone units and sulfonated pendant phenyl groups inhibits excessive water absorption in membranes, ensures efficient proton-conduction, and restrains the attack of radicals on the main chains. The combination of sulfonated pendant phenyl groups and twisted heterocyclic structures would enhance the oxidation stability and fuel-cell performance.
engineering, chemical,polymer science