Abstract:Surface modification of TiO2 with CuO or calcium phosphate (CaP) can result in enhancement in the photocatalytic activity for organic degradation. In this work, we report on a synergism between the cation and anion of copper phosphate (CuP) on the photocatalytic activity of TiO2, for phenol degradation in aerated aqueous suspension under UV light at wavelengths longer than 320 nm. Photocatalysts were prepared by mixing TiO2 and CuP powders in isopropyl alcohol, followed by drying at 90 degrees C. As CuP loading increased, the activity of the modified TiO2 first increased and then decreased The maximum activity was observed with the catalyst containing 0.1 wt % CuP, which was about 1.9-3.4 times that of bare TiO2 (anatase, rutile, and their mixture) and also exceeded that of the modified TiO2 with CuO or CaP. During five repeated tests, the catalyst activity was stable, without detectable leaching of cupric and phosphate ions into aqueous solution Solid characterization with several techniques including electron paramagnetic resonance (EPR) spectroscopy revealed that CuP particles at low loading were highly dispersed onto TiO2 as a kind of clusters, whereas the TiO2 phase, in different samples remained nearly unchanged in terms of the crystal structure, surface area, and crystallinity. Upon exposure to UV light, the EPR signal of Cu(II) in CuP or CuO-modifed TiO2 was unchanged in air but slightly decreased in N-2. Moreover, CuP-modified TiO2 showed a higher capacity than bare TiO2 and CuO- or CaP-modified TiO2 for the uptake of 2,4-dichlorophenol from water. It is proposed that cupric and phosphate ions act as an electron scavenger and organic sorbent, which facilitate electron and hole transfer, respectively. Their co-operation would significantly improve the efficiency of charge separation, and thus increase the rate of phenol degradation.

Dispersion of Metal Phthalocyanines on Surface of TiO2

Effect on Photocatalysed Property of TiO2 Thin Film by the Preparation of High-Purity Metal Phthalocyanin

Adsorption and assembly of copper phthalocyanine on cross-linked TiO2(110)-(1 x 2) and TiO2(210)

Copper(Ⅱ) Phthalocyanine Tetrasulfonate Sensitized Nanocrystalline TiO_2: in-Situ Hydrothermal Synthesis and Photocatalysis under Visible Light

Adsorption and Assembly of Copper Phthalocyanine on Cross-Linked TiO<sub>2</sub>(110)-(1 × 2) and TiO<sub>2</sub>(210)

Copper(II) phthalocyanine tetrasulfonate sensitized nanocrystalline TiO2: in-situ hydrothermal synthesis and photocatalysis under visible light

Adsorption behavior of iron phthalocyanine at the initial stage on Cu(100) surface

Preparation And Properties Of The Copper Phthalocyanine Tetrasulfonate Sensitized Tio2 Photocatalyst

Copper(II) phthalocyanine tetrasulfonate sensitized nanocrystalline titania photocatalyst: Synthesis in situ and photocatalysis under visible light

A monolayer dispersion study of titania-supported copper oxide

Differences in the Adsorption of FePc on Coinage Metal Surfaces

Electronic structures of CuPc on a Ag(110) surface

Spectrum Characterization and Fine Structure of Copper Phthalocyanine-Doped Tio2 Microcavities

Hydrothermal in Situ Preparation of the Copper Phthalocyanine Tetrasulfonate Modified Titanium Dioxide Photocatalyst

Interaction Between Tetrasulfophthalocyanines and Collidal TiO2 Andinterfacial Electron Transfer

Influence of Titanium Oxide on the Surface Interactions of MO (m=cu and Ni)/γ-Al2O3 Catalysts

Enhanced Surface Plasmon by Clusters in TiO2-Ag Composite

Dispersion and Stabilization of Photocatalytic TiO 2 Nanoparticles in Aqueous Suspension for Coatings Applications

Cooperative Effect Between Cation and Anion of Copper Phosphate on the Photocatalytic Activity of Tio2 for Phenol Degradation in Aqueous Suspension

Isoelectric Point-Controlled Preferential Photodeposition of Platinum on Cu2O-TiO2 Composite Surfaces

Ultrathin films of tetrasulfonated copper phthalocyanine-capped titanium dioxide nanoparticles: fabrication, characterization, and photovoltaic effect