Preparation of blue long afterglow phosphors CaAl2O4 : Eu2+, Nd3+ and its luminescent properties

Yuhua Wang,Lei Wang,Shuihe Zhang

2005-01-01

Abstract:A series of single-phase long afterglow phosphors Ca(1-x-y) Al2O4: Eu-x(2+), Nd-y(3+) (0 <= x <= 0. 045, 0 <= y <= 0.0037) were prepared by the traditional solid state reaction method and their photoluminescence were investigated. Intense blue emission of the samples was observed with a broad hand peak at about 440 nm, which is due to the 4f (6)5d -> 4f(7) transition of Eu2+. The effect of different rare earth contents on the afterglow proper-ties was investigated and the optimum content of Eu2+ and Nd3+ are x = 0.00125 and y = 0.0025 re spectively. Initial brightness and persistent afterglow time of the corresponding sample is over 1200 mcd/m(2) and more than 1000 min. 60 min later, its brightness is still over 10 mcd/m(2). Thermoluminescence and posi tron annihilation methods were used to investigate the effect of Nd3+ and Eu2+ co-doping on their luminescent properties.