Effect Of Polymer Latexes With Varied Glass Transition Temperature On Cement Hydration
Zichen Lu,Xiangming Kong,Chaoyang Zhang,Yi Cai,Qing Zhang,Yanrong Zhang
DOI: https://doi.org/10.1002/app.45264
IF: 3
2017-01-01
Journal of Applied Polymer Science
Abstract:Influence of styrene-acrylate latexes with varied glass transition temperature (T-g) on cement hydration was studied and the mechanism was analyzed. Results show that polymer latexes with varied T-g retard cement hydration to different extents. Specifically, low T-g polymer shows stronger retardation effect than the high T-g polymer. Despite similar surface charges, colloidal particles with lower T-g exhibit higher affinity to surface of cement grains than the high T-g polymer, indicated by the higher adsorption amount and denser covering layer. The low T-g polymer experiences particle packing, deforming, and film forming processes along with the consumption of water during cement hydration, which eventually produces a covering layer of polymer surrounding cement grains. However, for the high T-g polymer, film forming process is absent. Consequently, the higher adsorption amount and the film-formation process along with cement hydration are the two reasons for the stronger retardation effect of the low T-g polymer. (c) 2017 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2017, 134, 45264.