Thermal Diffusivity of Ordered Double Perovskite A(2)Femoo(6) (A = Ca, Sr and Ba)

XJ Liu,QJ Huang,DL Niu,S Xu,SY Zhang

DOI: https://doi.org/10.1088/0256-307x/21/11/057

2004-01-01

Chinese Physics Letters

Abstract:Thermal diffusivity has been investigated in ordered double perovskite Sr2FeMoO6 by means of transient surface grating technique in the temperature range of 300-450 K. The thermal diffusivity shows an appreciable decrease from 39 mm(2)/s at 300 K to 37 mm(2)/s at 360 K in the ferromagnetic phase, and then steeply drops to 10 mm(2)/s with further increasing temperature above the critical temperature T-c similar to 380 K. Such an abrupt decrease of the thermal diffusivity has been ascribed to the structural phase transition at T-c. We further investigate the lattice effect on the thermal diffusivity in A(2)FeMoO(6) (A = Ca, Sr and Ba) by substitution of Ca2+ or Ba2+ ions for Sr2+ ions at 300 K. We find that the thermal diffusivity increases from 35 mm(2)/s for A = Ca to 41 mm(2)/s for A = Ba. Considering the chan-e of the Fe-O-Mo bond angle from 152.4degrees for A = Ca to 180degrees for A = Ba, the increased thermal diffusivity for Ba compound has been ascribed to the enhanced hybridization between transition-metal d and oxygen p states due to the larger Fe-O-Mo bond angle and hence the wider one-electron bandwidth W.