Abstract:The optical, vibrational, and photoluminescence properties of Ho3+‐doped boro‐bismuth‐germanate glasses were studied. Upon 450 nm excitation, intense green emission around 550 nm was observed in low Ho3+‐doped glasses, whereas high Ho3+ doping leads to the concentration quenching effect; the reasons behind the quenching of emission intensity and decay time of 5S2 + 5F4 (Ho3+) level have been discussed. The studied glasses could be a good choice for display devices and green emission applications. Holmium (Ho3+)‐doped boro‐bismuth‐germanate glasses having the chemical composition (30‐x)B2O3 + 20GeO2 + 20Bi2O3 + 20Na2O + 10Y2O3 + xHo2O3, where x = 0.1, 0.5, 1.0, and 2.0 mol% were prepared by melt‐quenching technique. The prepared glasses were examined for thermal, optical, vibrational, and photoluminescent properties. The prepared glasses were found to be thermally very stable. The optical bandgap and Urbach energies of 0.1 mol% Ho2O3‐doped boro‐bismuth‐germanate glass were calculated to be 3.3 eV and 377 MeV, respectively, using the absorption spectrum. The Judd–Ofelt analysis was performed on the 0.1 mol% Ho2O3‐doped glass and compared the obtained parameters with literature. The branching ratio (β) and emission cross‐section (σem) of the green band were determined to be 0.7 and 0.24 × 10−20 cm2, respectively. Under 450 nm excitation, a strong green emission around 550 nm was observed and assigned to the (5S2 + 5F4) → 5I8 (Ho3+) transition. Upon an increase of Ho2O3 content from 0.1 to 2.0 mol%, the intensities of all observed emission bands as well as decay time of the (5S2 + 5F4) → 5I8 transition have been decreased gradually. The reasons behind the decrease in emission intensity and decay time were discussed. The strong green emission suggests that these glasses may be a better option for display devices and green emission applications.

Observation of 1.5μm Photoluminescence and Electroluminescence from a Holmium Organic Complex

Holmium porphyrin compound liquid crystals: Synthesis and properties

Synthesis, Crystal Structure, and Luminescent Properties of a New Holmium(III) Coordination Polymer Involving 2,5-Dihydroxy-1,4-terephthalic Acid Dianion as Ligand

Optical, vibrational, and photoluminescence properties of holmium‐doped boro‐bismuth‐germanate glasses

Electrolummescence from (5)do -> F-7(J) and D-5(1) -> F-7(J) (J=0-4) Transitions with A Europium Complex As Emitter

Luminescent Properties of Organic–inorganic Hybrid Monoliths Containing Rare-Earth Complexes

Sensitized Holmium Upconversion Emission in LiNbO3 Triply Doped with Ho3+, Yb3+, and Nd3+

Emissions of 1.20 and 1.38 μm from Ho3+-doped lithium-barium-bismuth-lead oxide glass for optical amplifications

Near- and Mid-Infrared Photoluminescence in Ho3+ Doped and Ho3+–Yb3+ Codoped Low-Phonon-energy Germanotellurite Glasses

Novel Holmium (Ho) and Praseodymium (Pr) ternary complexes with fluorinated-ligand and 4,5-diazafluoren-9-one

Strong Dependence of Upconversion Luminescence on Doping Concentration in Holmium and Ytterbium Co-Doped Y 2 O 3 Phosphor

Electroluminescence from {sup 5} D {sub 0}{yields}{sup 7} F {sub J} and {sup 5} D {sub 1}{yields}{sup 7} F {sub J}(J= 0 4) transitions with a europium complex as emitter

Luminescence of a Europium (III) Complex Containing 4-N-octyloxydibenzoylmethane Ligands Doped Poly(methylmethacrylate)

1.54 Mu M Infrared Photoluminescence and Electroluminescence from an Erbium Organic Compound

Synthesis, Crystal Structure and Luminescent Property of a New Holmium(Iii) Coordination Polymer Involving 2,5-Dihydroxy-1,4-Terephthalic Acid as Ligand

Electroluminescence from 5D0 → 7FJ and 5D1 → 7FJ (J = 0–4) transitions with a europium complex as emitter

Near-infrared luminescence from sol-gel materials doped with holmium(III) and thulium(III) complexes

[Spectroscopy Parameters of Ho3+ in Ho3+ : FOG and Ho3+ : FOV].

Elucidating Surface and Bulk Emission in 3D Hybrid Organic–Inorganic Lead Bromide Perovskites

Photoluminescence Properties of Dinuclear Lanthanide Complexes in Visible and Near-Infrared Region

1.54 Μm Near-infrared Photoluminescent and Electroluminescent Properties of a New Erbium (III) Organic Complex