Low-Dimensional Organic Metal Halide Hybrids with Excitation-Dependent Optical Waveguides from Visible to Near-Infrared Emission
Siqin Wu,Bo Zhou,Dongpeng Yan
DOI: https://doi.org/10.1021/acsami.1c03926
2021-05-27
Abstract:Molecular luminescent materials with optical waveguide properties have wide application prospects in the fields of sensors, filters, and modulators. However, designing and synthesizing optical waveguide materials with unique morphology, high emissive efficiency, and tunable optical properties in the same solid-state system remains an open challenge. In this work, we report new types of morphological one-dimensional (1D) organic metal halide hybrid micro/nanotubes and micro/nanorods, which exhibit excitation-dependent optical waveguide properties from visible to near-infrared (NIR) regions with low-loss coefficient and high emissive efficiency during the propagation process. Strong intermolecular interactions within the hybrid systems could effectively reduce the nonradiative transition and improve quantum efficiency. Photophysical studies and theoretical calculations demonstrate that the color-tunable emission can be attributed to the coexistence of locally excited states and charge-transfer states. Utilizing excitation-dependent optical waveguide emission ranging from visible to NIR regions, we fabricate an optical wavelength converter to transfer short-wavelength into long-wavelength emission with multichannels. Furthermore, an optical logic gate system was designed based on the tunable emission properties of the 1D metal halide micro/nanotubes. Therefore, this work provides not only a facile process to synthesize 1D organic metal halide hybrids with excitation-dependent optical waveguide properties but also a new way to advance photofunctional logic computation at the micro/nanoscale.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c03926?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c03926</a>.Angles between pyridyl and phenyl in Zn-Bpeb, Cd-Bpeb, and Pb-Bpeb (Figure S1); packing of Cd-Bpeb projected along the <i>a</i>-axis and <i>c</i>-axis, the four-coordinate structure, π–π stacking, and hydrogen bonds (Figure S2); FT-IR spectra and thermogravimetric analysis (TGA) curves of Bpeb, Zn-Bpeb, Cd-Bpeb, and Pb-Bpeb (Figures S3, S4); SEM images of Zn-Bpeb and Cd-Bpeb (Figure S5); normalized PL excitation spectra and PL spectra of Bpeb in solid state and in solution state (Figure S6); normalized excitation-dependent PL spectra of Zn-Bpeb, Cd-Bpeb, and Pb-Bpeb crystals at room temperature (Figure S7); corresponding positions of the different emissions in the chromaticity coordinates diagram of Zn-Bpeb, Cd-Bpeb, and Pb-Bpeb (Figure S8); PL excitation spectra of Cd-Bpeb crystals at room temperature (Figure S9); excitation-dependent normalized PL spectra of Pb-Bpeb crystals (Figure S10); time-resolved fluorescence decay of Bpeb, Zn-Bpeb, Cd-Bpeb, and Pb-Bpeb in solid-state (Figure S11); comparison of PLQY values for Zn-Bpeb, Cd-Bpeb, and Pb-Bpeb (Figure S12); measurement profiles of PLQY for Bpeb, Zn-Bpeb, Cd-Bpeb, and Pb-Bpeb (Figure S13); and PDOS of the components in Zn-Bpeb, Cd-Bpeb, and Pb-Bpeb (Figure S14, S15) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c03926/suppl_file/am1c03926_si_001.pdf">PDF</a>)Cd-Bpeb (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c03926/suppl_file/am1c03926_si_002.cif">CIF</a>)Zn-Bpeb (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c03926/suppl_file/am1c03926_si_003.cif">CIF</a>)Pb-Bpeb (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c03926/suppl_file/am1c03926_si_004.cif">CIF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology