A study on mechanical properties and morphology of methylenediphenyl diisocyanate chain extending poly(D,L-lactide)/hydroxyapatite composite

刘芳,金艳,贾德民,吴小华,郭陨圆,王迎军
DOI: https://doi.org/10.3321/j.issn:1673-8225.2004.02.030
2004-01-01
Abstract:Aim: To investigate the effect of compression-extruding conditions and methylenediphenyl diisocyanate(MDI) content on mechanical properties and morphology of poly (D, L-lactide) /hydroxyapatite composite (PDLLA/HA) by utilizing self-designed compression-extruding equipment. Methods: Poly(D, L-lactide) (PDLLA) and MDI chain-extending PDLLA/HA were prepared in the presence of stannous(II) octoate respectively, and scanning electron microscopy(SEM) was used to observe fracture surfaces of composites. Results: Bending strength of PDLLA/HA composite got maximum at processing temperature of 100 °C, heat and pressure preservation time of 45 min and its bending strength almost unchanged with further increasing time of heat and pressure preservation. But its bending modulus had no influence with increasing time of heat and pressure preservation. When molar ratio of -NCO group in MDI to -OH group in PDLLA was 1: 1, both bending strength and bending modulus of PDLLA/HA composite got the maximum. SEM results showed that there were a lot of parallel oriented structure of fibrils to long axis in bending fracture surface and longitudinal split surface. Conclusion: The compression-extruding technique compelled PDLLA/HA composite to form oriented structure and MDI chain-extending can increase molecular weight of PDLLA/HA composite, so its mechanical properties are enhanced. The compression-extruding conditions and MDI content obviously affect mechanical properties and morphology of PDLLA/HA composite.
What problem does this paper attempt to address?