Al2O3-coated honeycomb cordierite-supported CuO for simultaneous SO2 and NO removal from flue gas: Effect of Na 2O additive

Qingya Liu,Zhenyu Liu,Zhenping Zhu,Guoyong Xie,Yanli Wang

2004-01-01

Abstract:Effect of Na2O additive in an Al2O3-coated cordierite honeycomb ceramic-supported CuO catalyst on simultaneous SO 2 and NO removal activities was studied at 400 °C. Results show that SO2 removal activity increases with increasing sodium loading from 0 to 2.0 wt % but decreases with further increasing sodium loading to 3.0 wt %, while NO removal activity monotonically decreases with increasing sodium loading, from 99 to 65%, due to increased NH3 oxidation activity. Mechanism of the effect of Na2O additive on SO2 removal activity is studied using N2 adsorption, scanning electron microscopy (SEM), energy-dispersive X-ray (EDX), and X-ray powder diffraction (XRD). Results show that Na2O additive (at sodium loadings of 1.0-2.0 wt %) inhibits the formation of Al-Si-O species and improves the distribution of CuO, which limits pore plugging and increases BET surface area of the catalyst. These behaviors account for the promoting effect of Na2O additive on SO2 removal activity. However, with increasing sodium loading from 2.0 to 3.0 wt %, more well-crystallized CuO are observed, which leads to a lower utilization rate of copper and thus SO2 removal activity. Chemical analysis and XRD results indicate that for the catalyst without Na2O additive, only CuSO4 is formed, whereas for the catalysts containing Na2O, the adsorbed SO2 exist in three forms: CuSO 4, NaCu2(SO4)2OH· H 2O, and Na2SO4.