Ti-O/Ti-N Biomedical Gradient Films Synthesized by Metal Vacuum Arc Plasma Deposition and Thermal Oxidation
Yongxiang Leng,Han Sun,Ping Yang,Junying Chen,Guojiang Wan,Jin Wang,Nan Huang
2003-01-01
Abstract:In the last two decades, low temperature isotropic pyrolytic carbon (LTIC) has been the best material for fabricating artificial heart valves. However, the blood compatibility of LTIC is not sufficient for prolonged clinical use. As a result, patients must continuously take anti-coagulation medication to prevent thrombus formation. Hence, the development of a material with better blood compatibility and mechanical properties is a real necessity faced by the biomedical community. Rutile type titanium oxide ceramics and TiO2 films prepared by thermal oxidation and ion beam assisted deposition, respectively, generally have blood compatibility better then that of LTIC, But its mechanical properties are not adequate for fabricating artificial heart valves. Titanium nitride is commonly used as a wear and corrosion resistant coating on cutting tools, machine components, and also biomaterials, due to its superior mechanical and chemical properties including high hardness, low wear coefficient and chemical stability. In this work, TiO/Ti-N films were synthesized on 1Cr18Ni9Ti substrates. Ti-N films were deposited on 1Cr18Ni9Ti substrate by metal vacuum arc deposition. Then the as-deposited Ti-N films were oxidized at 600° for 25min to synthesize Ti-O/Ti-N gradient film. As mentioned, in the complex Ti-O/Ti-N structure, the presence of Ti-O improves the blood compatibility and the main effect of Ti-N is to improve the mechanical properties. The composition, microstructure and mechanical properties of Ti-N and Ti-O/Ti-N gradient film were examined by XPS, XRD, microhardness tester and ball-on-disk wear test. Using a constant-potential method, the anodic polarization of the films has been measured, and the corrosion resistance properties of the films have been evaluated. XRD analysis research suggests that there are TiN and TiO2 phases in Ti-O/Ti-N gradient film. XPS analysis shows that the composition of the Ti-O film surface is entirely TiO2 oxidized completely. The result of microhardness experiments show that Ti-N film and Ti-O/Ti-N gradient film deposited on 1Cr18Ni9Ti can improve the hardness of stainless steel, being approximately 2-3 times greater than that of the substrate. The wear resistance of Ti-O/Ti-N gradient films has been clearly improved, approximately doubled. The results of electrochemical experimental measurements suggest that the corrosion resistance of TiN films on stainless steel, as-deposited by metal vacuum arc plasma deposition, was slightly improved, which contrasts with stainless steel. But the corrosion resistance properties of Ti-O/Ti-N gradient films grown by thermal oxidation was dramatically decreased, because of defects in the thermal oxidation surface of the films, for example, loose, cavity and so on, which are generated by the heat treatment. The solution to this was to synthesize Ti-O by plasma oxidation and form compact films.