Abstract:The microstructure and mechanical properties of Fe-0.19C-1.46Mn-1.50Si, a low-carbon hot-rolling direct quenching and partitioning steel, were investigated, and particular emphasis was placed on the effects of the rolling temperature and the subsequent cooling method. Once rolling occurred above the recrystallization temperature, the grain size of prior austenite could be reduced from ∼88.2 to ∼11.8 μm. The corresponding packet and block sizes of martensite could be reduced from ∼17.6 to ∼4.3 μm and from ∼9.0 to ∼1.8 μm, respectively, after a typical two-step quenching and partitioning (Q&P) treatment following rolling immediately. Once rolling occurred below the recrystallization temperature, deformed prior austenite with a grain length and width of ∼150 and ∼60 μm, respectively, were obtained. Consequently, only the block size would be reduced to ∼1.9 μm. The volume fraction of retained austenite (RA), which was ∼11% in the specimens, was not significantly affected by the rolling temperature. Further, if the typical two-step Q&P treatment was replaced by air cooling after the rolled specimen was quenched to the martensitic start temperature, the volume fraction of RA in the specimen was reduced to ∼7.4%, and the corresponding carbon depletion degree in the martensitic matrix was decreased as well. Tension and impact tests indicated that the cooling method was more critical than the rolling temperature for determining the mechanical properties. The presence of sufficient amounts of RA and carbon depletion in the refined martensitic matrix contribute to the strong strain hardening and energy absorption capabilities of the steel together. As a result, rolling at a temperature that was slightly higher than the recrystallization temperature combined with the typical two-step Q&P treatment could be an optimized process to obtain excellent comprehensive mechanical properties. In particular, the ductile-to-brittle transition temperature (DBTT) could be reduced from −10°C to −30°C.

Effects of Heat Treatment on Structures and Properties of High Speed Steel Rolls

Investigations on Heat Treatment of a High-Speed Steel Roll

Development of Powder Metallurgy High Speed Steel

A Study of Heat Treatment of High‐boron High‐speed Steel Roll

Effect of Heat Treatment on Microstructure and Properties of Powder Metallurgy High-Speed Steel Prepared by Hot Isostatic Pressing

Effect of Heat Treatment on Structure and Properties of B Alloyed High Speed Steel for Rolling Mill Rolls

On Microstructure and Performance of Tempered High-Boron High-Speed Steel Roll

Effects of Heat Treatment Process on Microstructure and Mechanical Properties for Extra-Thick High-Strength Steel Plate

The Effect of Long-Time Austenization on the Wear Resistance and Thermal Fatigue Properties of a High-Speed Steel Roll

Effect of heat treatment on mechanical properties of 1500MPa high strength wear-resistant steel

Effect of Quenching and Tempering Treatment on Microstructure and Mechanical Properties of CSS-42L Bearing Steel

Effect of Cycling Heat Treatment on the Microstructure and Properties of H13 Steel Prepared for Hot-Extrusion Die

Effect of Quenching Process on Microstructure of a HSLA Steel

Microstructure and mechanical properties of a low-carbon HDQ&P steel

Effect of Rapid Heating and Quenching on Microstructure and Mechanical Properties of High Strength Low Alloy Steel

Effect of Ti Addition on the Microstructure and Properties of A High Speed Steel Roll

Microstructural Evolution, Behavior of Precipitates, and Mechanical Properties of Powder Metallurgical High-Speed Steel S390 During Tempering

Effect of hot stamping and quenching & partitioning process on microstructure and mechanical properties of ultra-high strength steel

Improving the Mechanical Properties of Hot Rolled Low-Carbon Copper-Containing Steel by Adjusting Quenching Roll Speed

Effect of Double Quenching on Microstructure and Impact Toughness of a High Strength Low Alloy Steel

Study on Heat Treatment of Multi-Element Low Alloy Wear-Resistant Cast Steel