Preparation and Characterization of Tin Catalysted ZnO Twin-crystal Nanowires
DONG Jing-bing,CHENG Yao,WAN Jian-guo,HAN Min,WANG Guang-hou
DOI: https://doi.org/10.3321/j.issn:1000-7032.2006.05.028
2006-01-01
Abstract:ZnO is a wide band gap oxide semiconductor material with important and potential applications in sensor, transducer, surface acoustic wave devices, and optoelectronic devices, etc. In the past several years, various methods have been developed for synthesizing the ZnO nanowires. Among these methods, Vapor- liquid-solid (VLS) growth mode is widely used because it does not demand complex apparatus or sophisticated techniques and one can easily synthesized the ZnO nanowires by the catalyzing process of the metal liquid drop in the tip of the nanowires. In this work, based on the VLS growth mechanism, we successfully prepared the twin-crystal Sn catalysted ZnO nanowires with uniform shape and wurtzite structure by a simple method of thermal evaporation of a mixture of SnO powder and Zn powder under the pure N_2 flow and O_2 flow. The pu- rity, composition, microstructrue and crystallinity of the as-prepared ZnO twin-crystal nanowires were investigated by XRD, HRTEM, SEM and SAED. According to SEM images, we observed that the as-synthesized ZnO nanowires were straight and uniform, and were 100~200 nm in diameter and several tens of micrometers in length, some even reaching millimeter level. TEM images and element analysis results verified that the spherical particle on the top of the nanowire was tin metal grain which played the role of catalyst in the process of nanowire growth. These suggested that the growth of ZnO twin-crystal nanowires was controlled by VLS mechanism. HRTEM images confirmed the twin-crystal structure of the nanowires. According to the SAED images, we made sure that the ZnO twin-crystal nanowires grew along [0110] direction and the twin-crystal plane was (101-3). The relationship between the twin-crystal lattice was analyzed by the dark field images and the bright field images. We also explained the VLS growth mechanism of the nanowires.