Abstract:This article reports the successful synthesis of mesoporous hydroxyapatite, Ca-10(PO4)(6)(OH)(2) (denoted HA) using cationic surfactant as the template. The wide-angle (2theta > 10degrees) diffraction data revealed characteristic peaks of HA, where a hexagonal lattice structure can be deduced. The lattice structure is found in space group P6(3)/m, the parameters of which are in excellent agreement with reference data; i.e. a = b = 0.9418 nm, c = 0.6884 nm. For small angle diffraction (2theta < 10&DEG;), the characteristic peaks occur at 2θ values of 3.30, 5.75, 7.25 and 8.30&DEG;, indicating the presence of atomic planes with a periodical spacing of 2.677 nm. Nitrogen adsorption indicated a pore size distribution of approximately 3 nm, and a corresponding pore volume of 0.0113 cm(3) g(-1), hence the volume ratio of the mesopores was found to be &SIM;0.036. SEM micrographs reveal a rod-like structure of HA, possessing a thickness of about 50-100 nm and length ranging from 500 to 1000 nm, while TEM micrographs revealed that nano-channels are formed within the rod-like structure. These nano-channels align in a lengthwise direction within the rods, consistent with the cavities being generated by the removal of "organic" CTAB templating structure during calcination. The channels have dimensions of around 3.5 nm and the spaces between the nano-channels are filled with an ordered crystalline HA structure. Comparing the pore size and the spacing between neighboring channels, the pore volume ratio of each rod was calculated to be &SIM;0.029, which is in agreement with the result from gas adsorption. A probable mechanism is that CTAB-PO43- mixtures form rod-like micelles, which contain many PO43- groups on the surface, and in the presence of Ca2+, Ca-9(PO4)(6) clusters are preferentially condensed on the rod-shaped micellar surface due to the conformation compatibility between the identical hexagonal shapes of the micelles and Ca-9(PO4)(6) clusters. The micelles act as nucleating points for the growth of HA crystals. During the thermal incubation stage, CTAB-HA complexes are produced and they coalesce to form a stable three-dimensional rod-like structure. The morphology of the final product shows about 10 layers of HA crystal grows on one micelle during the reaction in water.

Synthetic mechanism of hydroxyapatite nanoparticles via AOT inverse microemulsions

A Novel Method to Synthesize Hydroxyapatite Coating with Hierarchical Structure

Synthesis of Hydroxyapatite Mediated by Amphiphilic Block Copolymer PS112-b-PAA38

Synthesis of Hydroxyapatite Mediated by Amphiphilic Block Copolymer PS<sub>112</sub>-b-PAA<sub>38</sub>

Hydrothermal synthesis of nano-hydroxyapatite crystals

Evolution of the magnesium incorporated amorphous calcium phosphate to nano-crystallized hydroxyapatite in alkaline solution

Controllable Synthesis Of Spherical Nano Hydroxyapatites And Their Effects On Growth And Osteogenic Differentiation Of Bone Marrow Derived Mesenchymal Stem Cells

The Preparation of Hydroxyapatite Nanowires and Nanorods Via Aliphatic Micelles As Soft Templates

Synthesis of α-calcium sulfate hemihydrate submicron-rods in water/n-hexanol/CTAB reverse microemulsion

Hydroxyapatite nanostructure material derived using cationic surfactant as a template

Conformations of satellite DNAs.

The Ultrasonic Assisted Synthesis of Nano-Hydroxyapatite and Mwnt/Hydroxyapatite Composites

Nucleation and growth of hydroxyapatite nanocrystals by hydrothermal method

Controllable Synthesis of Different Size Hydroxyapatite Nanoparticles and Their Biological Effects on Osteoblast-Like Cells

Crystallization of smooth amorphous calcium phosphate microspheres to core-shell hydroxyapatite microspheres

Aqueous Preparation of Highly Dispersed Hydroxyapatite Nanorods for Colloidal Liquid Crystals

Physical exercise attenuates age‐associated reduction in endothelium‐reparative capacity of endothelial progenitor cells by increasing CXCR4/JAK‐2 signaling in healthy men

FTIR, XRD, SEM and solid state NMR investigations of carbonate-containing hydroxyapatite nano-particles synthesized by hydroxide-gel technique

Role of triton X-100 and hydrothermal treatment on the morphological features of nanoporous hydroxyapatite nanorods

Effect of pH on the In Vitro Biocompatibility of Surfactant-Assisted Synthesis and Hydrothermal Precipitation of Rod-Shaped Nano-Hydroxyapatite

A simple method to controlled synthesis of nano hydroxyapatite in different particle size