Abstract:The synthesis of partially substituted silicon hydroxyapatite (Si-HAp) nanopowders was systematically investigated via the microwave-assisted hydrothermal process. The experiments were conducted at 150 °C for 1 h using TMAS (C4H13NO5Si2) as a Si4+ precursor. To improve the Si4+ uptake in the hexagonal structure, the Si precursor was supplied above the stoichiometric molar ratio (0.2 M). The concentration of the TMAS aqueous solutions used varied between 0.3 and 1.8 M, corresponding to saturation levels of 1.5–9.0-fold. Rietveld refinement analyses indicated that Si incorporation occurred in the HAp lattice by replacing phosphate groups (PO43−) with the silicate (SiO4−) group. FT-IR and XPS analyses also confirmed the gradual uptake of SiO4− units in the HAp, as the saturation of Si4+ reached 1.8 M. TEM observations confirmed that Si-HAp agglomerates had a high crystallinity and are constituted by tiny rod-shaped particles with single-crystal habit. Furthermore, a reduction in the particle growth process took place by increasing the Si4+ excess content up to 1.8 M, and the excess of Si4+ triggered the fine rod-shaped particles self-assembly to form agglomerates. The agglomerate size that occurred with intermediate (0.99 mol%) and large (12.16 mol%) Si contents varied between 233.1 and 315.1 nm, respectively. The excess of Si in the hydrothermal medium might trigger the formation of the Si-HAp agglomerates prepared under fast kinetic reaction conditions assisted by the microwave heating. Consequently, the use of microwave heating-assisted hydrothermal conditions has delivered high processing efficiency to crystallize Si-HAp with a broad content of Si4+.

The Ultrasonic Assisted Synthesis of Nano-Hydroxyapatite and Mwnt/Hydroxyapatite Composites

Hydrothermal synthesis of nano-hydroxyapatite crystals

Controllable Synthesis Of Spherical Nano Hydroxyapatites And Their Effects On Growth And Osteogenic Differentiation Of Bone Marrow Derived Mesenchymal Stem Cells

Synthesis of Hydroxyapatite Mediated by Amphiphilic Block Copolymer PS112-b-PAA38

Ultrafast Synthesis and Characterization of Carbonated Hydroxyapatite Nanopowders Via Sonochemistry-Assisted Microwave Process.

A simple method to synthesize nanocrystalline hydroxyapatite

Synthesis and Characterization of Hydroxyapatite Nanobelts and Nanoparticles

Synthesis of Mesoporous Hydroxyapatite Nanoparticles Using a Template-Free Sonochemistry-Assisted Microwave Method

Preparation of Nano Hydroxyapatite Powders by Sonochemistry Method

Synthesis and Property Study of Hydroxyapatite Nanoparticles by Microemulsions

Preparation of Nano-Hydroxyapatite in Lyotropic Lamellar Liquid Crystal

Synthesis and Characterization of Nano Hydroxyapatite Particles

Controlled synthesis and transformation of nano-hydroxyapatite with tailored morphologies for biomedical applications

Controllable Synthesis of Spherical Hydroxyapatite Nanoparticles Using Inverse Microemulsion Method

Self-assembly of Nano-Hydroxyapatite on Multi-Walled Carbon Nanotubes

Effect of Ultrasound Irradiation on the Synthesis of Hydroxyapatite/Titanium Oxide Nanocomposites

Nucleation and growth of hydroxyapatite nanocrystals by hydrothermal method

FTIR, XRD, SEM and solid state NMR investigations of carbonate-containing hydroxyapatite nano-particles synthesized by hydroxide-gel technique

Hydrothermal Microemulsion Synthesis of Stoichiometric Single Crystal Hydroxyapatite Nanorods with Mono-Dispersion and Narrow-Size Distribution

Preparation and Characterization of Hydroxyapatite Nanotubes

Preparation of Silicon Hydroxyapatite Nanopowders under Microwave-Assisted Hydrothermal Method