Study on Mechanical Behavior and Microstructure Evolution of Ti1023 Alloy During High Temperature Plastic Deformation
Zhigang GAO,Min WANG,Peng ZHANG,Wen CHEN,Jiajun WANG,Hongzhen GUO,Zekun YAO
DOI: https://doi.org/10.14158/j.cnki.1001-3814.2016.11.001
2016-01-01
Abstract:The true stress-true strain curves were obtained through the isothermal compression experiment of Ti1023 alloy.And the microstructure evolution law of the alloy after deformation and heat treatment was studied.The results show that in the process of high temperature deformation,the flow stress of Ti1023 alloy is sensitive to deformation parameters,and the stress-strain curves show a certain regularity under different deformation conditions.Under the condition of low temperature and high strain rate,the stress-strain curves show dynamic recrystallization characteristics.And the curves are dynamic recovery characteristic at high temperature.With the increase of defo~ation temperature,the amount of α-phase precipitation gradually decreases and the shape is gradually evolved from the equal axis or sheet to a long strip.With the increase of strain rate,the α-phase morphology gradually evolves into a long strip and the size decreases.Different morphologies of the α-phase have different effects on the properties of the alloys,and the microstructure of good comprehensive performance can be obtained after the deformation atthe middle temperature zore (760-780 ℃).