Microstructure and Properties of Ultrafine-Grained Aluminum-Based Alloy Processed by Equal Channel Angular Pressing

王立忠,王经涛,郭成,陈金德

DOI: https://doi.org/10.3321/j.issn:0253-987X.2004.05.005

2004-01-01

Abstract:Ultrafine-grained aluminum-based alloy was fabricated via equal-channel angular pressing (ECAP) and microstructural evolution at different passes of ECAP was researched. The results reveal that the microstructures evolve from an array of elongated dislocation cells with grain size less than 1 μm separated by boundaries having low angles of misorientation into an array of reasonably finer bands of subgrains separated by high-angle boundaries with increasing severe plastic deformation. The grain size is reduced from 50 μm in the initial state to 0.2 μm after a total of 8 passes of ECAP. The grain size is within 0.2-0.3 μm while annealed at 150°C for 4 min to 240 min. A maximum elongation of 370% is achieved at 500°C with an initial strain rate of 10-3 s-1 in a tension test, showing a fine super-plasticity of the ultrafine-grained material.